牌号简介 About |
---|
AOC的Vipel K022系列是一种溶于苯乙烯的溴化双酚A环氧乙烯基酯树脂。VIPEL K022系列非常适合用于手工铺层、喷涂、纤维缠绕和拉挤加工,其中需要优异的机械性能和优异的耐化学药品和耐热性。Vipel K022-CN系列含锑产品。优点阻燃一些Vipel K022版本不需要三氧化二锑来满足ASTM E 84 I级火焰蔓延要求。机械性能Vipel K022适用于承受特别高静或动载荷的模具。乙烯基酯树脂具有优异的耐热性。通用的宽配方能力允许在许多过程中使用,并优化成本/性能。耐腐蚀Vipel K022对多种化学环境具有很高的抵抗力。请参阅AOC的“耐腐蚀树脂指南”,了解耐腐蚀信息或有关树脂适用于任何特定化学环境的问题,请联系AOC。 AOC's Vipel K022 series is a brominated bisphenol A epoxy vinyl ester resin dissolved in styrene. Vipel K022 series is ideally suited for use in hand lay-up, spray-up, filament winding and pultrusion processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required. Vipel K022-CN series contains antimony products. BENEFITS Fire Retardant Some Vipel K022 versions do not require antimony trioxide to meet ASTM E 84 Class I flame spread requirements. Mechanical Properties Vipel K022 is suitable for moldings that are subjected to particularly high static or dynamic loads. Vinyl ester resins have excellent resistance to sustained heat. Versatile Wide formulating capabilities allow for use in many processes and for optimization of cost/performance. Corrosion Resistance Vipel K022 is highly resistant to a number of chemical environments. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
39 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
114 | ℃ | ASTM D648 |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
火焰传播 flame propagation |
10.0 | ASTM E84 | |
Smoke Developed Smoke Developed |
650 | ASTM E84 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
13.0 | min | |
放热峰值 exothermic peak |
℃ | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 RVT,25℃ 25℃,Brookfield RVT |
Pa·s | ||
胶凝时间 Gelation time |
|||
25℃ 25℃ |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
陶氏杜邦裁员 节省30亿美元开支
2017-11-06 陶氏杜邦集团启动节省年度30亿美元成本计划,包括裁员、停厂。 本周四陶氏杜邦在声明中表示,全球裁员,关停工厂和资产,节省购买成本等方式将实现目标最大化。此外,该公司还批准回购40亿美元的股票。 这一举措显示了首席执行官埃德・布林为实现加快全球化学品巨头盈利速度的承诺,该公司于8月31日由陶氏化学和杜邦公司共同创建,计划在2019年初分成三部分。 此前许多分析师预计,为其重大项目的建设,陶氏将重新启动股票回购计划,以腾出资金。 桑福德伯恩斯坦. |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |