| 牌号简介 About |
|---|
| BRASKEM FLEXUS 7200XP是一种利用茂金属催化剂生产的线性低密度聚乙烯。它是专门为提供出色的加工性能而设计的。用这种方法制备的薄膜具有优异的机械和光学性能。它含有抗氧化添加剂。应用拉伸薄膜工艺：薄膜挤出的推荐加工条件约为220-270°C。最佳加工条件将根据所用设备的类型而变化，不能视为性能保证。 Braskem FLEXUS 7200XP is a Linear Low Density Polyethylene produced through metallocene catalyst. It was specially designed to provide outstanding processing performance. Films obtained with this grade show excellent mechanical and optical properties. It contains antioxidant additives. Applications Stretch films Process Recommended processing conditions for film extrusion about 220 - 270 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
产品描述 Product Description
用途：薄膜;拉伸缠绕;
加工条件：薄膜挤出 Film extrusion
性能特点： 抗氧化; 光学性能; 易加工; Excellent Processability,Optical performance,Inoxidizability
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
3.5 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD：25 µm，吹塑薄膜 1% secant, MD: 25 µ m, blow molded film |
180 | MPa | ASTM D882 |
|
1% 正割，TD：25 µm，吹塑薄膜 1% secant, TD: 25 µ m, blow molded film |
190 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
|||
|
25 µm，吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD：25 µm，吹塑薄膜 MD: 25 µ m, blow molded film |
g | ASTM D1922 | |
|
TD：25 µm，吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss 2 |
|||
|
60°，23.0 µm，吹塑薄膜 60 °, 23.0 µ m, blow molded film 2 |
ASTM D2457 | ||
|
透光率 Transmittance 2 |
|||
|
23.0 µm，吹塑薄膜 23.0 µ m, blow molded film 2 |
% | ASTM D1003 | |
|
雾度 Haze 2 |
|||
|
23 µm 23 µm 2 |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Cling（23.0 µm） Cling（23.0 µm） 3 |
g | ASTM D4649 | |
|
Puncture（23.0 µm） Puncture（23.0 µm） 3 |
g | ASTM D4649 | |
|
Retention Ending Force（23.0 µm） Retention Ending Force（23.0 µm） 3 |
g | ASTM D4649 | |
|
Retention Loss（23.0 µm） Retention Loss（23.0 µm） 3 |
% | ASTM D4649 | |
|
Retention Maximum Force（23.0 µm） Retention Maximum Force（23.0 µm） 3 |
g | ASTM D4649 | |
|
Ultimate Test（23.0 µm） Ultimate Test（23.0 µm） 3 |
% | ASTM D4649 | |
| 备注 |
|---|
| 2 75%Flexus7200XP + 25% LLDPE Octene |
| 3 3 layer coextruder, 75%Flexus7200XP + 25% LLDPE Octene |
|
【新闻资讯】查看全部 
华鲁恒升高端溶剂及尼龙66高端新材料项目开工
2022-02-28 2月25日下午，全省重大项目-山东华鲁恒升化工股份有限公司高端溶剂及尼龙66高端新材料项目开工。 据介绍，该项目总投资41亿元，产品主要用于新能源电池、高强度材料等领域，具有 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付