牌号简介 About |
---|
BMC 620模塑料是一种矿物填充的玻璃纤维增强聚酯化合物,适用于压缩成型,填充器注射成型,具有良好的成型性、高冲击强度、优异的整体电气性能和阻燃性。典型应用包括压铸件、母线支架、断路器外壳、相分离器和接触器块的模铸替换件。BMC 620模塑料是一系列工业颜色的产品,以散装形式供应。 BMC 620 molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression, and stuffer injection molding It is characterized by good moldability high impact strength, excellent overall electrical properties and flame resistance. Typical applications include molded replacements for die castings, buss supports, circuit breaker housings, phase separators and contactor blocks. BMC 620 molding compound is produced in a range on industrial colors, and is supplied in bulk form. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.73 to 1.79 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:模压成型 MD: Compression molding |
0.26 to 0.38 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.14 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
模压成型 Compression Molding |
320 to 480 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,模压成型 1.8 MPa, unannealed, molded |
260 | ℃ | ASTM D648 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength 2 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
Inclined(Plane Tracking,2.5 kV) Inclined(Plane Tracking,2.5 kV) |
min | ASTM D2303 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
6.40 mm 6.40 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ASTM D638 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
巴氏硬度 Babbitt hardness 2 |
ASTM D2583 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部
齐鲁塑料厂春节时期聚乙烯等产品创产超万吨
2017-02-08 春节长假期间,齐鲁石化塑料厂精心组织安排生产,干部职工坚守工作岗位,认真操作,及时发现消除装置运行中遇到各类问题,节日期间,共生产产品19817吨,实现了安全稳定生产。 该厂认真落实公司有关春节放假的生产管理要求,把确保节日期间安稳生产放在首位,节前结合各装置实际制定了相应节日生产指南和事故应急预案,结合节前安全大检查对高压聚乙烯、苯乙烯、线性聚乙烯等各装置展开隐患排查,能整改的立即整改,暂不具备整改条件的制定严密防范措施,标注在节日生产指南中。该厂还重点落实各项防冻防凝措 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |