牌号简介 About |
---|
Andur M-33是一种低熔点MDI酯预聚物,在加工过程中密切关注处理程序和配方,生产出高质量的弹性体。这些弹性体在低温应用中表现很好。 |
技术参数 Technical Data | |||
---|---|---|---|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服 yield |
18.4 | MPa | ASTM D412 |
100% 应变 100% strain |
12.2 | MPa | ASTM D412 |
300% 应变 300% strain |
14.8 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
510 | % | ASTM D412 |
压缩形变 Compression deformation |
21 | % | ASTM D395 |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
储存稳定性 storage stability |
min | ||
脱模时间 stripping time |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 D Shaw's D |
ASTM D2240 | ||
压缩强度 compressive strength |
ASTM D695 | ||
2% 应变 2% strain |
MPa | ASTM D695 | |
5% 应变 5% strain |
MPa | ASTM D695 | |
10% 应变 10% strain |
MPa | ASTM D695 | |
15% 应变 15% strain |
MPa | ASTM D695 | |
20% 应变 20% strain |
MPa | ASTM D695 | |
25% 应变 25% strain |
MPa | ASTM D695 | |
50% 应变 50% strain |
MPa | ASTM D695 | |
泰伯耐磨性 Taber abraser |
mg | ASTM D1044 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
页岩气开发劲头猛烈已撼动塑料行业
2016-03-21 罗蒙斯特――Associates LLC塑料行业咨询公司总经理菲利普凯瑞否认页岩气的繁荣已经结束,他认为今天的真相未必是明天的真理,因为现状发展,曾经也无法预计。 目前,页岩气和天然气已经从根本上改变了美国看待能源消耗这一问题,正是观念的转变,推动了塑料产业的发展,也带来了前所未有的商机和投资风潮。 美国的页岩气开发正在受到水力压裂和水平钻井的推动,这让能源公司得以开发过去无法触及的领域。由此将增加以天然气为原料的乙烷和丙烷的供应,这些原料可作为石化原料。这 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |