牌号简介 About |
---|
10%玻璃纤维增强有核PBT/ASA,具有优异的机械性能、高尺寸稳定性和低密度。 10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/2C | ||
-30℃ -30℃ |
5.0 | kJ/m² | ISO 179/2C |
23℃ 23℃ |
6.0 | kJ/m² | ISO 179/2C |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/2U | ||
-30℃ -30℃ |
20 | kJ/m² | ISO 179/2U |
23℃ 23℃ |
45 | kJ/m² | ISO 179/2U |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
45 | J/m | ASTM D256 |
0℃ 0℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 9 |
kJ/m² | ISO 180-1A | |
0℃ 0℃ 9 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 9 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
-30℃ -30℃ 9 |
kJ/m² | ISO 180/1U | |
23℃ 23℃ 9 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 10 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 10 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ASTM D1525,ISO 306 | |
A50 A50 |
℃ | ASTM D1525,ISO 306 | |
B120 B120 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
ISO 11359-2 | ||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:23~60℃ MD:23~60℃ |
1/℃ | ISO 11359-2 | |
MD:23~150℃ MD:23~150℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:23~60℃ TD:23~60℃ |
1/℃ | ISO 11359-2 | |
TD:23~150℃ TD:23~150℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 , IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 , IEC 60250 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
填充物 Filler |
% | ASTM D229 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ISO 2039-2 | ||
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
|||
-- -- 2 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
-- -- 5 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 5 , 6 |
MPa | ISO 178 | |
-- -- 5 , 7 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
断裂,50 mm跨度 Fracture, 50 mm span 4 |
MPa | ASTM D790 | |
断裂弯曲应变 Fracture bending strain 8 |
% | ISO 178 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 , ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
200℃,3.80kg 200℃,3.80kg |
g/10min | ASTM D1238 | |
265℃,5.0kg 265℃,5.0kg |
g/10min | ASTM D1238 | |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
250℃,5 kg 250℃,5 kg |
cm³/10min | ISO 1133 | |
265℃,5 kg 265℃,5 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
熔体表观粘度 Apparent viscosity of melt |
|||
260℃,1500 sec^-1 260℃,1500 sec^-1 |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0,20 in/min |
3 类型 1, 0,20 in/min |
4 0,051 in/min |
5 0,079 in/min |
6 Break |
7 Yield |
8 2 mm/min |
9 80*10*4 |
10 80*10*4 mm |
【新闻资讯】查看全部
走私废塑料!青岛海关摧毁5个洋渣滓走私团伙
2017-03-07 多个犯罪团伙采取制作虚假单证伪报品名方式,从黄岛口岸走私“洋垃圾”在境内销售牟利,被青岛海关缉私一举摧毁。近日,青岛海关组织开展打击“洋垃圾”走私专项行动,共刑事立案5起,抓获犯罪嫌疑人19名,涉及走私废矿渣、废塑料7200余吨。 |
走私废塑料!青岛海关摧毁5个洋渣滓走私团伙 好几个团伙犯罪采用制做虚报报关单证伪报产品名方法,从青岛市黄岛区港口走私“洋垃圾”在地区市场销售牟取暴利,被青岛海关缉私一举催毁。近日,青岛海关机构进行严厉打击“洋垃圾”走私专项整治,共刑事立案5起,抓捕嫌疑人19名,涉及到走私废矿渣、废塑料7200余吨。 走私废塑料!青岛海关端掉五个洋垃圾走私犯罪团伙 2月24日,在中国海关总署缉私局统一指挥下,青岛海关进行了严厉打击“洋垃圾”走私专项整治,派出审理案件工作人员高达187人,多地同歩行動,对涉案人员企业场地进行搜察,对因涉嫌走私入境的固体废物储放场地及生产加工黑窝点开展查控,一举捣毁了五个走私废矿渣、废塑料团伙犯罪,当场扣留废矿渣海运集装箱88个,总共1700余吨。 核查,2016年至今,杭州市某公司为牟取不法权益,采用制做虚报报关单证伪报产品名方法自青岛市黄岛区港口走私国家严禁進口的废矿渣4200余吨,在地区市场销售牟取暴利。另外,好几家未获得国家环评资质的公司,违背国家要求,运用别人《限制进口可用作原料的固体废物进口许可证》走私進口废塑料3000余吨,在地区生产加工市场销售牟取暴利。据了解,废矿渣系国家严禁進口的固体废物,進口废矿渣不符国家生态环境保护操纵规范,违背《中华人民共和国固体废物污染环境防治法》及《固体废物进口管理办法》,非常容易对生态安全和身体健康造成不良影响。针对国家限定進口可作为原材料的废塑料等固体废物,沒有获得国家环评资质的公司或本人,运用别人许可证书走私進口的,因在生产制造获取运用全过程中沒有必需的污染治理设备,非常容易对本地自然环境导致环境污染威协。 近些年,洋垃圾从欧美国家等发展国家向在我国地区不法迁移的难题十分突显,对在我国生态环境保护和老百姓身心健康导致的伤害令人震惊。据了解,国外对固体废物开展解决必须很高的成本费,而运往中国转让卖出则能赚钱。为了更好地牟取爆利,许多中国公司挺而走险,在容许進口的废料中参杂一部分禁止入关的废料,即别名的’洋垃圾’,非常容易引起二次污染。中国海关将查控走私固体废物文件目录中的矿渣、矿灰及沉渣,轮胎胶粉,废塑料、废皮革制品、废纺织材料以及产品、废料电气产品、城市生活垃圾等做为关键,严厉查处货运物流方式隐匿、为报、请托或是贩卖别人许可证书件等方法走私固体废物非法活动,果断将有害危害物件截在国境以外,维护生态环境保护和人民大众身体健康。 来源于:搜狐网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。