牌号简介 About |
---|
Nucrel® 0902HC是乙烯-甲基丙烯酸共聚物树脂,通常由9 wt%甲基丙烯酸制成。该树脂可用于传统吹塑和铸膜挤出和共挤设备,设计用于处理聚乙烯树脂。 Nucrel® 0902HC is an ethylene-methacrylic acid copolymer resin, made nominally from 9 wt% methacrylic acid. The resin is available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | ASTM D792 |
密度 Density |
0.930 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.5 | g/10min | ISO 1133 |
190℃,2.16kg 190℃,2.16kg |
1.5 | g/10min | ASTM D1238 |
Methacrylic Acid Content Methacrylic Acid Content |
9.0 | wt% | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temperature |
℃ | ASTM D1525 | |
维卡软化温度 Vicat Softening Temperature |
℃ | ISO 306 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
冰点 freezing point |
|||
-- -- |
℃ | ISO 3146 | |
-- -- |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部 ![]()
济南炼化成功生产土工布聚丙烯专用料
2022-04-15 近日,由济南炼化、北化院、华北化销联合开发的YU28G聚丙烯专用料工业化试生产成功,该专用料分子量分布窄、可纺性优异、单丝强度高,可替代进口土工布聚丙烯专用料。 土工布即 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |