牌号简介 About |
---|
LNP Thermocomp RF00CSXZ是一种基于回收尼龙66树脂的化合物,含有60%的玻璃纤维。这种材料的附加特性包括:热稳定。又名:lnp*Thermocomp*化合物RF-100-12 HS产品再订购名称:RF00CSXZ LNP THERMOCOMP RF00CSXZ is a compound based on Recycled Nylon 66 resin containing 60% Glass Fiber. Added features of this material include: Heat Stabilized. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.72 | g/cm³ | ASTM D792 |
密度 Density |
1.72 | g/cm³ | ISO 1183 |
收缩率 Shrinkage |
ISO 294-4 | ||
TD:24 hrs TD:24 hrs |
0.40 | % | ASTM D955 |
MD:24 hrs MD:24 hrs |
0.30 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
0.44 | % | ISO 294-4 |
MD:24 hrs MD:24 hrs |
% | ISO 294-4 | |
吸水率 Water Absorption |
|||
24hr,50% RH 24hr,50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
断裂 fracture |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Flexural Modulus |
MPa | ASTM D790 | |
弯曲模量 Flexural Modulus |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength 3 |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 3 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength 3 |
|||
23℃ 23℃ 3 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 4 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 4 |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 80*10*4 |
4 80*10*4 mm |
【新闻资讯】查看全部 ![]()
碳排放权交易首个履约期将至 碳市场放量
2021-12-16 搜料网资讯: 截至12月13日,全国碳市场碳排放配额(CEA)累计成交量8494.82万吨,累计成交额35.14亿元。全国碳排放权交易市场自今年7月16日启动上线交易以来,市场总体运行平稳,随着 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |