牌号简介 About |
---|
双轴取向聚丙烯(BOPP)薄膜是用热封聚烯烃共聚物在两侧共挤而成的具有双轴拉伸性能的高速包缠薄膜。OLS65/80/100适用于需要特殊包装外观和包装紧密性的高速覆盖和水平填模应用。广泛的密封范围和机械性能使OLS薄膜特别适合要求高的镁和光学介质、糖果和茶叶应用。 High Speed Overwraping Film with Shrink Tightening Properties Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with heat sealable polyolefinic copolymers. OLS65/80/100 are suitable for high speed overwrapping and horizontal form-fill applications where exceptional pack appearance and wrap tightness are required. The wide sealing range and enchanced machine performance make OLS films particularly suited to demanding magnectic and optical media, confectionery and tea applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
收缩率 Shrinkage rate |
内部方法 | ||
MD:80℃,1 min MD:80℃,1 min |
3.7 | % | 内部方法 |
MD:120℃,1 min MD:120℃,1 min |
7.0 | % | 内部方法 |
TD:80℃,1 min TD:80℃,1 min |
3.5 | % | 内部方法 |
TD:120℃,1 min TD:120℃,1 min |
11 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态,外层/外层 With oneself - dynamic, outer/outer layers |
0.30 | ASTM D1894 | |
与自身 - 静态,外层/外层 Compared to itself - static, outer/outer layers |
ASTM D1894 | ||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus 2 |
ASTM D882 | ||
1% 正割,MD 1% secant, MD |
MPa | ASTM D882 | |
1% 正割,TD 1% secant, TD |
MPa | ASTM D882 | |
拉伸强度 tensile strength 3 |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
密封强调 Sealing emphasis 4 |
N/mm | 内部方法 | |
始封温度 Initial sealing temperature 5 |
℃ | 内部方法 | |
透氧率 Oxygen permeability |
|||
23℃,0% RH 23℃,0% RH |
cm³·mm/m²/atm/24 hr | ASTM F1927 | |
水气透过率 Water vapor transmittance |
ASTM F1770 | ||
23℃,85% RH 23℃,85% RH |
g/m²/24 hr | ASTM F1770 | |
38℃,90% RH 38℃,90% RH |
g/m²/24 hr | ASTM F1770 | |
薄膜厚度 film thickness |
内部方法 | ||
用量 dosage |
m²/kg | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
20° 20° |
ASTM D2457 | ||
雾度 Haze 6 |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10%/min |
3 50%/min |
4 225°F; 1sec; 15lb/in² |
5 2secs; 15lb/in² |
6 Wide angle, 2.5° |
【新闻资讯】查看全部
汉高与青岛轨道交通产业示范区签署战略合作协议
2021-07-25 搜料网资讯: 近日,汉高 粘合剂 业务部与青岛轨道交通产业示范区管委会签署战略合作协议。汉高将与青岛轨道交通产业示范区在轨道交通以及 碳纤维 新材料、轨道车体及零部件、轨 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |