| 牌号简介 About |
|---|
| SURPASS® FPs016-C是一种线性低密度聚乙烯材料,。 该产品在北美洲有供货,加工方式为:薄膜挤出。 SURPASS® FPs016-C的主要特性有: 加工助剂 抗氧化剂 可接触食品 良好的抗撕裂强度 良好的韧性 典型应用领域包括: 电影 食品接触应用 涂覆应用 SURPASS® FPs016-C is a Linear Low Density Polyethylene material. It is available in North America for film extrusion. Important attributes of SURPASS® FPs016-C are: Antioxidant Food Contact Acceptable Good Tear Strength Good Toughness Octene Comonomer Typical applications include: Coating Applications Film Food Contact Applications |
产品描述 Product Description
用途：薄膜;层压板;
加工条件：薄膜挤出 Film extrusion
性能特点： 熔体强度好; 低速凝固晶点; 机械强度好-撕裂; 抗氧化; 辛烯共聚单体; 食品接触; 低密度; 韧性好; Good flexibility,Low speed solidification point,Food contact compliance,Inoxidizability,Good melt strength,Low density,Good tear strength,Octene copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.916 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.65 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
25 | µm | |
|
割线模量 Secant modulus |
|||
|
1% 正割，TD，25 µm，吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
138 | MPa | ASTM D882 |
|
1% 正割，MD，25 µm，吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
126 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
|||
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
TD，屈服，25 µm，吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
MD，屈服，25 µm，吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
|||
|
TD，断裂，25 µm，吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
|
MD，断裂，25 µm，吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
|||
|
25 µm，吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709-A | |
|
撕裂强度 tear strength |
|||
|
TD，25 µm，吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
|
MD，25 µm，吹塑薄膜 MD, 25 µ m, blow molded film |
g | ASTM D1922 | |
|
密封起始温度 Sealing starting temperature 2 |
|||
|
25 µm，吹塑薄膜 25 µ m, blow molded film 2 |
℃ | ||
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
ASTM D2457 | ||
|
45°，25 µm，吹塑薄膜 45 °, 25 µ m, blow molded film 3 |
ASTM D2457 | ||
|
45°，25 µm，吹塑薄膜 45 °, 25 µ m, blow molded film 4 |
ASTM D2457 | ||
|
雾度 Haze |
ASTM D1003 | ||
|
25 µm，吹塑薄膜 25 µ m, blow molded film 3 |
% | ASTM D1003 | |
|
25 µm，吹塑薄膜 25 µ m, blow molded film 4 |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
低摩擦穿刺 Low friction puncture |
|||
|
吹塑薄膜，25.0 µm Blow molded film, 25.0 µ m |
J/cm | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Temperature at which a 2 mil film achieves a seal strength of 4.4N/13mm. 0.5 sec dwell, 0.27 N/mm² bar pressure, 305 mm/min pull speed |
| 3 LDPE Blended |
| 4 100% LLDPE |
|
【新闻资讯】查看全部 
餐饮业“撤离”！麦当劳、星巴克、可口可乐等宣布暂停在俄业务
2022-03-10 当地时间3月8日，美国餐饮连锁公司麦当劳宣布，将暂时关闭俄罗斯境内的850家门店，但是会继续支付员工工资，旗下的麦当劳叔叔之家慈善基金（Ronald McDonald House Charities）也将继续运 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付