牌号简介 About |
---|
Elite*5500g增强聚乙烯树脂是通过InSite*技术生产的共聚物。它提供了可加工性、低热封起始温度、包装完整性、光学性能和撕裂强度的特殊组合。一种用于食品和特种包装薄膜的高性能密封剂,在吹塑和铸膜挤出设备上具有优异的密封性能、可填缝性、光学性和撕裂强度的组合,易于加工,符合:美国FDA FCN 424欧盟,2011年10月加拿大HPFB无异议,请参考法规了解完整细节。 ELITE* 5500G Enhanced Polyethylene Resin is a copolymer produced via INSITE* Technology. It offers an exceptional combination of processability, low heat seal initiation temperature, package integrity, optical properties, and tear strength. A high performance sealant for food and specialty packaging films Outstanding combination of seal performance, caulkability, optics, and tear strength Easy processability on blown and cast film extrusion equipment Complies with: U.S. FDA FCN 424 EU, No 10/2011 Canadian HPFB No Objection Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.914 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
膜刺穿强度 Membrane puncture strength |
5.65 | J | 内部方法 |
膜刺穿力 Membrane puncture force |
62.3 | N | 内部方法 |
膜耐刺穿性 Membrane puncture resistance |
J/cm³ | 内部方法 | |
膜强度 Membrane strength |
ASTM D882 | ||
MD MD |
J/cm³ | ASTM D882 | |
TD TD |
J/cm³ | ASTM D882 | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD 1% secant, MD |
MPa | ASTM D882 | |
2% 正割,MD 2% secant, MD |
MPa | ASTM D882 | |
1% 正割,TD 1% secant, TD |
MPa | ASTM D882 | |
2% 正割,TD 2% secant, TD |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ASTM D1922 | |
TD TD |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
海南省加快田间废弃物污染治理
2016-01-29 地膜等农业投入品在促进海南农业提质增效的同时,也不断造成环境污染和土壤结构破坏。为保障农业可持续发展,海南省加快农业投入品田间废弃物污染治理,力争“十三五”内实现“不留一块废膜在田头”。 海南农业投入品田间废弃物主要包括地膜和农药包装物两大类。海南每年使用地膜面积约300万亩,主要为冬种瓜菜,按每亩5公斤计算,年投入量约1.5万吨;每年农药使用量约1.2万吨,产生的废弃包装物约1000吨。 “目前海南对这两类废弃物尚未进行有效回收和综合利用, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |