牌号简介 About |
---|
Electroblend® PBT-1901是一种玻璃纤维增强抗静电聚对苯二甲酸丁二醇酯化合物,具有较高的机械性能和较低的收缩性能。 Electroblend® PBT-1901 is a glass fiber reinforced antistatic polybutylene terephthalate compound characterized by high mechanical with lower shrinkage properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.51 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.20 到 0.60 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
85.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.5 | % | ASTM D638 |
弯曲模量 Bending modulus |
7200 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部 ![]()
突发!埃克森美孚将关闭其在新加坡的头号裂解装置
2022-04-20 根据CommoPlast的市场消息,埃克森美孚新加坡公司计划于2022年4月25日关闭其在新加坡裕隆岛的1号裂解装置,具体原因不详。 该裂解装置是旧石化综合体的一部分,年产量为90万吨乙烯和 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |