| 牌号简介 About |
|---|
| Viton® GFLT-600S氟弹性体是一种67%的氟、过氧化固化的低温氟弹性体。GFLT-600S采用了最新的技术，先进的聚合物结构（APA），其中包括一个新的过氧化物固化位点以及优化的分子量分布。特性能够非常快速地固化到高固化状态，与Viton GFLT相比，改善了低温性能；改善了模具释放/污染性能；改善了65 Mooney过氧固化FKM的模具流动性和较低的剪切敏感性；具有高延伸率的优良物理性能，包括原始和老化的热、流体和低延伸率。耐温性与氟橡胶相当，GFLT提高了耐水性/降低了水中体积膨胀，无论是低还是无后固化，都具有良好的抗压缩永久变形性能。 Viton® GFLT-600S fluoroelastomer is a 67% fluorine, peroxide-cured, low temperature fluoroelastomer. GFLT-600S utilizes the latest technology, Advanced Polymer Architecture (APA), which includes a novel peroxide cure site along with an optimized molecular weight distribution. Features Cures exceptionally fast to a high state of cure Similar to improved low temperature properties compared to Viton® GFLT Improved mold release/mold fouling properties Improved mold flow and less shear sensitivity for a 65 Mooney peroxy cured FKM Excellent physical properties with high elongation, both original and aged Heat, fluids, and low temperature resistance comparable to Viton® GFLT Improved water resistance/lower volume swell in water Excellent compression set resistance with either low or no postcure |
产品描述 Product Description
颜色：白色
性能特点： 拉伸性能好; 尺寸稳定性好; 含脱模剂; 耐低温; 易加工; Excellent Processability,Good Dimensional Stability,Antifreeze,Good stripping performance,Good Tensile Strength
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.86 | g/cm³ | ASTM D792 |
|
门尼粘度 Mooney viscosity |
|||
|
ML 1+10，121℃ ML 1+10，121℃ |
65 | MU | ASTM D1646 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A，23℃ Shore A, 23 ℃ |
68 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 2 |
71 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 3 |
70 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 4 |
ASTM D2240 | ||
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
10% 应变 10% strain |
ASTM D412 | ||
|
23℃ 23℃ 5 |
MPa | ASTM D412 | |
|
23℃ 23℃ 6 |
MPa | ASTM D412 | |
|
23℃ 23℃ 7 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 8 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 9 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 10 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 11 |
MPa | ASTM D412 | |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
屈服，23℃ Yield, 23 ℃ 8 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 9 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 10 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 11 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
ASTM D412 | ||
|
断裂，23℃ Fracture, 23 ℃ 8 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 9 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 10 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 11 |
% | ASTM D412 | |
|
撕裂强度 tear strength 12 , 13 |
|||
|
150℃ 150℃ 12 , 13 |
kN/m | ASTM D624 | |
|
压缩形变 Compression deformation |
ASTM D395B | ||
|
200℃，22 hr 200℃，22 hr |
% | ASTM D395B | |
|
200℃，22 hr 200℃，22 hr 14 |
% | ASTM D395B | |
|
200℃，70 hr 200℃，70 hr |
% | ASTM D395B | |
|
200℃，70 hr 200℃，70 hr 14 |
% | ASTM D395B | |
|
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积变化 Volume change |
ASTM D471 | ||
|
23℃，168 hr，C级标准燃料 23 ℃, 168 hr, C-grade standard fuel |
% | ASTM D471 | |
|
23℃，168 hr，in M15（Fuel C/Methanol 85/15） 23℃，168 hr，in M15（Fuel C/Methanol 85/15） |
% | ASTM D471 | |
|
23℃，168 hr，甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
|
23℃，168 hr，在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
|
150℃，168 hr，在ASTM 105油中 150 ℃, 168 hr, in ASTM 105 oil |
% | ASTM D471 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 508 mm/min, Aged 70 hr at 275°C |
| 3 508 mm/min, Aged 70 hr at 250°C |
| 4 508 mm/min |
| 5 20 in/min |
| 6 20 in/min, 老化 ASTM 105 Oil 168 hr 在 302°F |
| 7 20 in/min, 老化 70 hr 在 482°F |
| 8 20 in/min, 老化 70 hr 在 527°F |
| 9 B 模具 |
| 10 Nicked |
| 11 Postcured for 2 hr at 232°C |
| 12 老化 ASTM 105 Oil 168 hr 在 302°F |
| 13 老化 70 hr 在 482°F |
| 14 老化 70 hr 在 527°F |
|
【新闻资讯】查看全部 
普利司通重启法国工厂
2021-08-08 搜料网资讯： 近日，普利司通宣布，其于今年4月关闭的法国Bthune工厂将重新启用。 欧洲汽车维修和移动公司Mobivia与法国翻新专家Black Star本月签署协议，在普利司通的支持下，合作伙伴 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |