牌号简介 About |
---|
Vinnolit® K 725 F是由氯乙烯接枝聚丙烯酸酯(ACR)聚合而成的自由流动粉末。该产品含有大约50%的ACR。Vinnolit® K 725 F是一种提高聚氯乙烯薄膜、片材和型材冲击强度的改性剂。使用Vinnolit® K 725 F制造的物品显示出极低的应力美白,适合外部应用。Vinnolit® K 725 F可储存在筒仓中。 Vinnolit K 725 F is a free-flowing powder produced by graft polymerization of vinyl chloride onto polyacrylate (ACR). The product contains roughly 50 % ACR. Vinnolit K 725 F is a modifying agent which increases the impact strength of PVC films, sheets and profiles. Articles manufactured with Vinnolit K 725 F show very low stress-whitening and are suitable for exterior applications. Vinnolit K 725 F may be stored in silos. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表观密度 Apparent density |
0.50 | g/cm³ | ISO 60 |
ACR Content ACR Content |
50 | % | |
挥发物 Volatiles |
< 0.30 | % | ISO 1269 |
颗粒大小分布 Particle size distribution |
ISO 4610 | ||
-- -- 2 |
> 70 | % | ISO 4610 |
-- -- 3 |
< 1.0 | % | ISO 4610 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 retained on 0.063 mm screen |
3 retained on 1.000 mm screen |
【新闻资讯】查看全部
塑料模具之模坯锻造知识讲解
2016-07-05 1、模具零件锻造的目的 模具零件坯料准备时锻造的目的有两个: (1)获得一定的几何形状; (2)改善材料的组织性能和加工性能。 模具中一般的结构件(如固定板、拉料板等)以第一目的为主,而主要的工作零件(如凸模、凹模等)则两项目的兼有。通过锻造获得模块坯料几何形状的方法,其灵活性极强。基本可满足模块坯料规格和尺寸多样性的要求,具有节省材料、缩短工时等优点。 对于模具中的主要零件,由于其热处理、质量和使用寿命等方面 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |