牌号简介 About |
---|
MFE-11是一种性能优良、耐腐蚀的双酚A环氧乙烯基酯树脂。性能中等粘度,用玻璃纤维有效浸湿,良好的空气干燥,表面干燥45分钟内具有优异的耐腐蚀性,特别是耐碱性。峰值放热低,收缩率低,韧性好。制作厚件时不要破裂。劳埃德注册了。符合FDA第21号法规CFR 177.2420的规定,在正确配制和固化后,可重复用于食品接触材料。适用于化工储罐、管道、船舱及整体防腐树脂砂浆地面、花岗岩、耐火砖等的勾缝材料,金属或混凝土结构的玻璃钢保护面衬片。可用于手工铺层、拉挤、喷涂和缠绕工艺。 MFE-11 is a bisphenol-A epoxy vinyl ester resin with high performance and excellent corrosion resistance. PROPERTIES Moderate viscosity, effectively wet out with glass fiber Good air drying, surface drying in 45 min Excellent corrosion resistance, especially to alkali. Low peak exotherm, low shrinkage, superior toughness. Do not crack when making thick parts. Lloyd's Registered. Complies with FDA regulation 21 CFR 177.2420, when properly formulated and cured, for repeated use in food contact materials. APPLICATION Chemical storage tank, pipeline, cabin and the jointing material of integral anti-corrosive resin-mortar flooring, granite and anti-proof brick, etc. Liner and flake of FRP protective surface of metal or concrete structure. Can be used in hand lay-up, pultrusion, spray up and filament winding process. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
酸值 acid value |
6.00 到 12.00 | mg KOH/g | |
固体含量 Solid content |
59 到 65 | % | |
粘度 viscosity |
|||
25℃ 25℃ |
0.3 到 0.5 | Pa·s | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
6.0 到 14.0 | min | |
放热峰值 exothermic peak |
130 到 140 | ℃ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-- -- 2 |
MPa | ASTM D790 | |
-- -- 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
-- -- 2 |
MPa | ASTM D790 | |
-- -- 3 |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 2 |
|||
1.8 MPa,未退火 1.8 MPa, unannealed 2 |
℃ | ASTM D648 | |
热稳定性 thermal stability |
|||
80℃ 80℃ |
day | ||
胶凝时间 Gelation time |
|||
25℃ 25℃ |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Casting |
3 FRP |
【新闻资讯】查看全部
模具企业竞争力决胜要素催生快速响应测量零碎
2016-06-13 随着现代模具制造工业迅速发展,模具行业市场竞争日趋激烈,缩短加工周期、降低制造成本、提高模具精度成为模具制造企业在竞争中胜出的三大关键因素。模具测量技术的发展尤为同行关注,国际模具及五金塑胶产业供应商协会负责人罗百辉在最近的企业访谈中指出,一个典型的模具企业,除了提升模具的生产制程能力,还需要精度高、功能强、通用性好的检测工具,固定式测量机就成为大多数模具企业质量检测环节首选的经典测量设备。 随着模具制造业的发展,不同的测量技术和测量设备根据模具制造的不同特点应运而生。从模 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |