牌号简介 About |
---|
软性和非卤化阻燃挤出级,用于评估UL 62 SPE和Nispe配置的电缆护套等应用。阻燃性能满足UL 1581 VW-1要求。90C或105C温度等级由UL 62 TPE类别定义。85肖氏A硬度。通常在标准挤压设备上进行的加工。使用0.12 mm x 20绞合铜导线在2.0 mm电线上进行的UL 1581试验。 Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as cable jacket of UL 62 SPE and NISPE configurations. Flame retardant performance capable of meeting UL 1581 VW-1 requirement. 90C or 105C temperature rating as defined by UL 62 TPE category. 85 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.01 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,10.0kg 250℃,10.0kg |
16 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -40.0 | ℃ | ASTM D746 |
Heat Deformation(121℃) Heat Deformation(121℃) 6 |
5.0 | % | UL 1581 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
1.9E+16 | ohms·cm | ASTM D257 |
介电强度 Dielectric strength |
|||
2 mm,在油中 2 mm in oil |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
VW-1 VW-1 |
UL 1581 | ||
烟雾密度 Smoke density |
ASTM E662 | ||
Flame,0.5 mm plaque,Ds,max Flame,0.5 mm plaque,Ds,max |
|||
Non-Flame,0.5 mm plaque,Ds,max Non-Flame,0.5 mm plaque,Ds,max |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,30 秒 Shore A, 30 seconds |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | UL 1581 | |
断裂 fracture 1 |
MPa | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 2 |
MPa | UL 1581 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | UL 1581 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 4 |
% | UL 1581 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 5 |
|||
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 2.0 in/min |
3 After 7 days |
4 0.49 in/min |
5 250 g |
【新闻资讯】查看全部
科莱恩后续项目将陆续上马
2017-07-19 科莱恩化工(惠州)有限公司,是由瑞士科莱恩集团在中国投资的第一个环氧乙烷衍生物工厂。公司成立于2009年,总投资9300万美元,占地8万平方米,设计产能10万吨表面活性剂,是科莱恩集团特种工业与消费品单元在亚太区投资最大、技术含量最高的一个项目。一期的产品主要是工业级表面活性剂,二期产品主要有个人护理用品、化妆品级别的表面活性剂,特别是活性原料药和辅料药,是国内目前唯一获得医药产品生产资质的化工企业。 项目名片 在省、市、区的积极协调和大力配合下,科莱恩化工 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |