| 牌号简介 About |
|---|
| 简介：Braskem flexus7200是一种线性低密度聚乙烯，茂金属乙烯-己烯共聚物，采用气相法生产。它是专门为提供出色的加工性能而设计的。用这种级别获得的薄膜显示出良好的抗冲击性和抗刺穿性。它含有抗氧化添加剂。用途：拉伸薄膜；衬里；低密度聚乙烯和高密度聚乙烯混合物；通用包装。 Braskem Flexus7200 is a Linear Low Density Polyethylene, metallocene ethylene-hexene copolymer, produced by gas phase process. It was specially designed to provide outstanding processing performance. Films obtained with this grade show excellent impact and puncture resistances. It contains antioxidant additives. Applications: Stretch films; liners; LDPE and HDPE blends; packages for general use. Process: Recommended processing conditions for film extrusion about 220 - 270 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
产品描述 Product Description
用途：薄膜;衬里;包装;拉伸缠绕;混合;
加工条件：薄膜挤出 Film extrusion
性能特点： 抗氧化; 共聚物; 己烯共聚单体; 冲击性能好; 抗穿孔性; 易加工; Excellent Processability,High impact resistance,Inoxidizability,Copolymer,Puncture Resistant,Hexene copolymers
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
3.5 | g/10min | ASTM D1238 |
|
厚度 thickness |
20.0 | g/min | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
割线模量 Secant modulus |
180 | MPa | ASTM D882 |
|
割线模量 Secant modulus |
190 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
|||
|
断裂，薄膜 Fracture, thin film |
MPa | ASTM D882 | |
|
拉伸强度 tensile strength |
|||
|
断裂，薄膜 Fracture, thin film |
MPa | ASTM D882 | |
|
薄膜断裂伸长率 Elongation at break of thin film |
% | ASTM D882 | |
|
薄膜断裂伸长率 Elongation at break of thin film |
% | ASTM D882 | |
|
撕裂强度 tear strength |
g/micron | ASTM D1922 | |
|
撕裂强度 tear strength |
g/micron | ASTM D1922 | |
|
落锤冲击 Drop hammer impact |
|||
|
25μm，吹塑薄膜 twenty-five μ m. Blown film |
g | ASTM D1709 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
雾 度 μm Haze μ M |
% | ASTM D1003 | |
|
光泽度 gloss |
% | ASTM D2457 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
金陵亨斯迈环氧丙烷项目顺利投产
2017-07-17 由中石化与美国亨斯迈在南京合资建设的环氧丙烷项目生产装置，近日实现一次开车成功，产出了合格环氧丙烷和甲基叔丁基醚。该项目自启动至今已4年多时间，此次顺利投产，对优化南京地区产业布局、加快江苏地区高附加值石化产业链的形成、促进新型节能环保材料的发展和高品质清洁油品的推广具有重要意义。 南京金陵亨斯迈新材料有限责任公司由中国石化股份有限公司和亨斯迈化工贸易(上海)有限公司合资组建，2012年11月在南京化工园注册成立，总投资49亿元，依托中国石化南京地区低碳烃资源优势和美国亨斯 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付