牌号简介 About |
---|
Lexan Exl9414T树脂LEXAN™ EXL9414T resin级是一种无卤阻燃聚碳酸酯,具有透明度、-40°C延展性和UL-94 V0等级,适用于注塑应用。卓越的冲击力、良好的流动性、透明的着色性以及薄壁火焰的可追溯性,使本产品成为薄壁应用的最佳候选产品。 LEXAN EXL9414T resin grade is a halogen-free flame retardant polycarbonate featuring transparency, -40 degree C ductility and UL-94 V0 rating for injection molding applications. Excellent impact combined with good flow, all transparent colorability for aesthetics and thin wall flame retradancy makes this product an excellent candidate for thin wall applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
13 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
12.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage |
|||
MD:3.2 mm MD:3.2 mm |
0.40 到 0.80 | % | 内部方法 |
吸水率 Water Absorption |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
0.12 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Flexural Modulus |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- 7 |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
|||
-- -- 8 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 9 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 10 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotched Impact strength 11 |
ISO 179/1eU | ||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 12 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 13 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength 14 |
ISO 180/1U | ||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 15 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temperature |
|||
B120 B120 |
℃ | ASTM D1525, ISO 306/B120 11 16 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~95℃ TD:-40~95℃ |
1/℃ | ASTM E831 | |
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
1.50 mm 1.50 mm |
|||
2.00 mm 2.00 mm |
|||
极限氧指数 Oxygen Index |
% | ISO 4589-2 | |
光学性能 OPTICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Light Transmission |
|||
2000 µm 2000 µm |
% | 内部方法 | |
雾度 Haze |
|||
2000 µm 2000 µm |
% | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 80*10*4 mm |
10 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
巴斯夫延续第六年荣膺“中国出色雇主”称号
2015-12-21 近日,巴斯夫连续第六年荣膺杰出雇主调研机构(CRF Institute)颁发的“中国杰出雇主”称号。同时,今年巴斯夫还获得了前程无忧颁发的2015中国最佳人力资源典范企业奖。这两大奖项认可了巴斯夫在人力资源管理各个方面的出色表现,包括职业发展、领导力培养、工作环境和文化以及薪酬和福利等。 “巴斯夫的‘创造化学新作用’战略的四大支柱中包括‘建立最佳团队’,体现了我们对员工的坚定承诺。为此,我们提供可靠的工作环境、着眼于长远的职业发展和终生学习的机会。”负责巴斯夫大中华区人力资 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |