牌号简介 About |
---|
Santoprene™ TPV原厂家埃克森美孚,现已被塞拉尼斯收购。
热塑性弹性体(TPE)系列中的一种柔软、可着色、特殊、不吸湿的热塑性硫化胶(TPV),特别配制成与ABS、PS、PC、PMMA、ASA、PET和PPO/PS共混物粘合,适用于需要硬/软组合的应用。该等级的山都平TPV与剪切有关,可在常规热塑性塑料设备上加工,用于注塑成型或挤出。基于聚烯烃且可回收的易拉罐制造流程。 A soft, colorable, specialty, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is especially formulated to bond to ABS, PS, PC, PMMA, ASA, PET and PPO/PS blends for applications where hard/soft combinations are required. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is polyolefin based and recyclable within the manufacturing stream. |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:TPV
性能特点: 防火阻燃等级HB; HB
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.04 | g/cm³ | ASTM D792 |
密度 Density Density |
1.04 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸应变 Tensile Strain Tensile Strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
600 | % | ASTM D412 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
600 | % | ISO 37 |
压缩永久变形 Compression Set |
|||
125℃,70 hr 125℃,70 hr |
55 | % | ISO 815 |
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness Shore hardness |
|||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
ISO 868 | ||
老化性能 Aging property |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 Change in Tensile Strength in Air Change in Tensile Strength in Air |
ASTM D573 | ||
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 Change in Tensile Strength in Air Change in Tensile Strength in Air |
ISO 188 | ||
100℃,168 hr 100℃,168 hr |
% | ISO 188 | |
125℃,168 hr 125℃,168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 Change in Ultimate Elongation in Air Change in Ultimate Elongation in Air |
ASTM D573 | ||
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 Change in Tensile Strain at Break in Air Change in Tensile Stress at Break in Air |
ISO 188 | ||
100℃,168 hr 100℃,168 hr |
% | ISO 188 | |
125℃,168 hr 125℃,168 hr |
% | ISO 188 | |
空气中硬度计硬度的变化率 Change in Durometer Hardness in Air Change in Durometer Hardness in Air |
ASTM D573 | ||
邵氏 A,100℃,168 hr Shaw A, 100 ℃, 168 hr |
ASTM D573 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 Change in Shore Hardness in Air Change in Shore Hardness in Air |
ISO 188 | ||
邵氏 A,100℃,168 hr Shaw A, 100 ℃, 168 hr |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr |
ISO 188 | ||
拉伸强度的变化率 Change in Tensile Strength Change in Tensile Strength |
ASTM D471 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
拉伸强度的变化率 Change in Tensile Strength Change in Tensile Strength |
ISO 1817 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ISO 1817 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
断裂时拉伸应力变化 Change in tensile stress during fracture Change in tensile stress during fracture |
ISO 1817 | ||
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ISO 1817 | |
邵氏硬度的变化率 Change rate of Shore hardness Change rate of Shore hardness |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在乙醇中,95% Shore A, 23 ℃, 168 hr, in ethanol, 95% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在盐酸中,10% Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在IRM 903 油中 Shaw A, 23 ℃, 168 hr, in IRM 903 oil |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在水中 Shaw A, 23 ℃, 168 hr, in water |
ASTM D471 | ||
邵氏硬度的变化率 Change rate of Shore hardness Change rate of Shore hardness |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在乙醇中,95% Shore A, 23 ℃, 168 hr, in ethanol, 95% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在盐酸中,10% Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在IRM 903 油中 Shaw A, 23 ℃, 168 hr, in IRM 903 oil |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在水中 Shaw A, 23 ℃, 168 hr, in water |
ISO 1817 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 | ||
1.10 mm 1.10 mm |
UL 94 | ||
2.90 mm 2.90 mm |
UL 94 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
古雷石化顺利打通外购原料供给乙烯装置流程
2022-01-21 搜料网资讯: 1月17日,古雷石化顺利打通外购丙烷、丁烷原料供给乙烯蒸汽裂解装置流程,进一步优化调整原料结构,为装置持续提质创效打下良好基础。 裂解原料选择是影响装置技术 |
古雷石化顺利打通外购原料供给乙烯装置流程 搜料网资讯:1月17日,古雷石化顺利打通外购丙烷、丁烷原料供给乙烯蒸汽裂解装置流程,进一步优化调整原料结构,为装置持续提质创效打下良好基础。 裂解原料选择是影响装置技术经济指标的重要因素,直接关系到目的产品收率、装置能耗、物耗等。公司乙烯装置裂解原料主要包括石脑油、液化石油气、外购丙烷和外购丁烷等。装置开车以来,受运输、储存等多方面条件限制,外购丙烷、丁烷原料供给流程一直未能打通,这成了制约装置提质创效的瓶颈。 随着丙烷、丁烷原料逐步具备投用条件,化工一部开始筹备投料各项准备工作。由于这两类原料均属于易燃易爆介质,一旦发生泄漏将造成严重后果,化工一部认真研究制定投料方案,严格落实系统气密、置换及隐患排查工作,全力保障投料工作安全。为了如期完成投料工作,工程师、班长带领裂解岗位员工连夜对系统进行置换,顶着冬夜里的寒风,手持作业工具在排放口逐个采样,反复调整置换时间,直至所有分析结果均合格。在相关岗位人员的共同努力下,装置成功引入原料并实现稳定运行。 该原料供给流程打通后,古雷石化可根据原料、产品市场和装置生产情况,及时调整原料加工占比,进而调整产品结构,不仅降低了单一原料的依赖性,也增加了生产计划的灵活度,有利于生产效益最大化。经测算,通过加工丙、丁烷原料,替代部分进口石脑油原料,乙烯及丙烯收率提高3%-5%,综合采购成本等因素,单吨原料加工效益提高约200元。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。