牌号简介 About |
---|
AMPLIFY™ EA 102功能聚合物是通过高压反应器生产的。这种乙烯-丙烯酸乙酯(EEA)共聚物具有很高的柔韧性,并赋予各种工程树脂低温韧性。该聚合物与其他聚烯烃具有良好的混合相容性。它可以用作聚烯烃和各种极性基板之间的连接层,例如金属、聚偏二氯乙烯(PVDC)、聚烯烃、纤维素、聚酯、聚碳酸酯、玻璃、箔、PVC、PET和聚苯乙烯。高性能包装应用聚合物改性连接层到聚偏二氯乙烯和聚烯烃优越的添加剂浓缩载体良好的热稳定性符合美国FDA 21 CFR 175.105美国FDA 21 CFR 177.1320(有限制)有关完整的详细信息,请参考法规。 AMPLIFY™ EA 102 Functional Polymer is produced via a high-pressure reactor. This ethylene-ethyl acrylate (EEA) copolymer exhibits high flexibility and imparts low temperature toughness to a wide range of engineering resins. This polymer demonstrates excellent blend compatibility with other polyolefins. It can be utilized as a tie layer between polyolefins and a variety of polar substrates, such as metal, polyvinylidiene chloride (PVDC), polyolefins, cellulose, polyester, polycarbonate, glass, foil, PVC, PET, and Polystyrene. High performance packaging applications Polymer modification Tie layer to PVDC and Polyolefins Superior additive concentrate carrier Excellent thermal stability Complies with U.S. FDA 21 CFR 175.105 U.S. FDA 21 CFR 177.1320 (with Restrictions) Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.931 | g/cm³ | ASTM D792 , ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
6.0 | g/10min | ASTM D1238,ISO 1133 |
共聚单体含量 Co monomer content 2 |
18.5 | % | ASTM D3594 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength 3 |
630 | kJ/m² | ASTM D1822 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
32.2 | ℃ | ASTM D648 |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 , ISO 306 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 , ISO 868 | ||
邵氏 A Shaw's A |
ASTM D2240 , ISO 868 | ||
邵氏 D Shaw's D |
ASTM D2240 , ISO 868 | ||
拉伸强度 tensile strength |
ASTM D638 , ISO 527-2 | ||
屈服 yield |
MPa | ASTM D638 , ISO 527-2 | |
断裂 fracture |
MPa | ASTM D638 , ISO 527-2 | |
拉伸应变 Tensile strain |
ASTM D638 , ISO 527-2 | ||
屈服 yield |
% | ASTM D638 , ISO 527-2 | |
断裂 fracture |
% | ASTM D638 , ISO 527-2 | |
弯曲模量 Bending modulus |
|||
2% 正割 2% secant |
MPa | ASTM D790B , ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 校准范围为 15 - 20% EA;路径长度已标准化;基板/薄膜厚度为 15 密尔;压机温度为 160°C |
3 类型 S |
【新闻资讯】查看全部
中化国际收购富比亚,进军塑料添加剂业务
2021-08-30 搜料网资讯: 中化国际宣布,公司已于8月26日完成对江苏富比亚化学品有限公司(以下简称富比亚)的收购,正式进军塑料添加剂业务。 江苏富比亚化学品有限公司 中化国际总经理刘 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |