| 牌号简介 About |
|---|
| CP741是一种低熔体流动速率的异相共聚物。具有广泛的分子量分布和通用的添加剂包装。CP 741具有低气味/味道转移、高熔融强度、良好的加工性能和优异的冲击强度，即使在低温下也能。应用：高冲击强度热成型包装；吹塑包装和一般技术零件；片材挤压 CP 741 is a low melt flow rate heterophasic copolymer. It has broad molecular weight distribution and general purpose additive package. CP 741 presents low odor/taste transfer, high melt strength, good processability and excellent impact strength even at low temperatures. Applications: Thermoformed packages with high impact strength; Blown packages and technical parts in general; Sheet extrusion with high impact resistance; Corrugated pipe extrusion for water drainage of sinks or washbasins. Processing: Thermoforming Blow Molding Extrusion |
产品描述 Product Description
用途：波形板;带子;食品包装;瓶子;管道系统;
加工条件：挤出 Extrusion
性能特点： 低透气性; 熔体强度好; 共聚物; 耐疲劳性好; 无毒; 冲击性能好; 易加工; Excellent Processability,High impact resistance,Low odor,Fatigue resistance,Good melt strength,Copolymer,Nontoxicity
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.895 | g/cm³ | ASTM D792 |
|
密度 Density |
0.895 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
0.80 | g/10min | ISO 1133 |
|
230℃，2.16kg 230℃，2.16kg |
0.80 | g/10min | ASTM D1238 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-20℃，注塑成型 -20 ℃, injection molding |
50 | J/m | ASTM D256 |
|
23℃，注塑成型 23 ℃, injection molding |
ASTM D256 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
|
-20℃，注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180 | |
|
23℃，注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火，注塑 1.8 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火，注塑成型 0.45 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
屈服，注塑成型 Yield, injection molding |
MPa | ISO 527-2 | |
|
屈服，注塑成型 Yield, injection molding |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
屈服，注塑成型 Yield, injection molding |
% | ISO 527-2 | |
|
屈服，注塑成型 Yield, injection molding |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
1% 正割，注塑成型 1% cut, injection molding |
MPa | ISO 178 | |
|
1% 正割，注塑成型 1% cut, injection molding |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level 2 |
ISO 2039-2 | ||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
|
【新闻资讯】查看全部 
武汉打造氢能枢纽城市
2022-04-16 近日，武汉市政府发布《武汉市人民政府关于支持氢能产业发展的意见》，加快推进全市能源结构清洁转型，以技术突破和产业培育为主线，打造创新研发、装备制造、示范应用协同发 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付