拉努芬HDI6507N是一种非常高密度的聚乙烯树脂,以注塑成型产品的高机械性能和良好的加工能力为主要特点。该树脂的注塑制品具有良好的刚性和优异的机械性能。对于需要良好刚性和机械性能的板条箱、容器、托盘和其他类似目标,建议使用Lanufene HDI 6507N。 LANUFENE HDI 6507N is a very high density polyethylene resin for injection molding of products with high mechanical properties and good process-ability as the main characteristics. The injection molded product from this resin characteristically exhibits good rigidity with outstanding mechanical properties. LANUFENE HDI 6507N is recommended for crates, containers, trays and other similar objectives where good rigidity and mechanical properties are needed. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.965 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
7.5 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) 2 |
|||
50 ℃,100%非离子表面活性剂,F50 50 ℃, 100% non-ionic surfactant, F50 2 |
40.0 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
极限 limit |
33.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
> 1000 | % | ASTM D638 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Non-slitted |
【新闻资讯】查看全部
前四月轻工主要行业投资保持两位数增长
2022-05-26 中国轻工业联合会近日公布前4月我国轻工业经济运行情况。数据显示,14月,轻工主要行业投资规模继续扩大,投资均保持两位数增长,其中农副食品加工、食品制造、酒饮料、皮革、 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |