| 牌号简介 About |
|---|
| Texin 245D树脂是一种芳香聚酯基热塑性聚氨酯，肖氏硬度约为43D*。它可以通过注塑成型进行加工；不建议使用挤压工艺。 |
产品描述 Product Description
用途：脚轮;齿轮;
性能特点： 抗冲击强度高; 耐油; 高灵活性; 耐低温; 耐磨性好; 韧性好; High impact strength,Antifreeze,Grease resistance,high wear resistance
,Good flexibility,High Flexibility
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
比重 Specific Gravity Specific Gravity |
1.21 | ASTM D792 | |
|
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
|
流向 Flow Direction Flow Direction |
0.008 | mm/mm | ASTM D955 |
|
横向流动 Cross-Flow Direction Cross Flow Direction |
0.008 | mm/mm | ASTM D955 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness Shore hardness |
43 | Shore D | ASTM D2240 |
|
泰伯耐磨性 Taber Abrasion Taber Abrasion |
70 | mg | ASTM D3489 |
|
Bayshore Resilience Bayshore Resilience |
% | ASTM D2632 | |
|
拉伸强度 Tensile Strength Tensile Strength |
MPa | ASTM D412 | |
|
拉伸应力 Tensile Stress Tensile Stress |
|||
|
50% 50% |
MPa | ASTM D412 | |
|
100% 100% |
MPa | ASTM D412 | |
|
300% 300% |
MPa | ASTM D412 | |
|
拉伸伸长率 Tensile Elongation Tensile Elongation |
% | ASTM D412 | |
|
弯曲模量 Flexural Modulus Flexural Modulus |
|||
|
70℃ 70℃ |
MPa | ASTM D790 | |
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
撕裂强度 tear strength Tear strength |
kN/m | ASTM D624 | |
|
压缩永久变形 Compression Set |
|||
|
22h，100℃ 22h，100℃ |
% | ASTM D395 | |
|
22h，70℃ 22h，70℃ |
% | ASTM D395 | |
|
22h，23℃ 22h，23℃ |
% | ASTM D395 | |
|
压缩强度 Compressive Strength Compressive Strength |
|||
|
2% 2% |
MPa | ASTM D575 | |
|
5% 5% |
MPa | ASTM D575 | |
|
10% 10% |
MPa | ASTM D575 | |
|
15% 15% |
MPa | ASTM D575 | |
|
20% 20% |
MPa | ASTM D575 | |
|
25% 25% |
MPa | ASTM D575 | |
|
50% 50% |
MPa | ASTM D575 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
|
23℃ 23℃ |
ASTM D256 | ||
|
-23℃ -23℃ |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Brittle Temperature Brittle Temperature |
℃ | ASTM D746 | |
|
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
℃ | ||
|
相对温度指数 Relative Temp Index(RTI) Relative Temperature Index (RTI) |
|||
|
电气 elec Electrical Elec |
℃ | UL-746B | |
|
机械冲击 Mechanical w/ Impact Mechanical w/Impact |
℃ | UL-746B | |
|
无机械冲击 Mechanical w/o Impact No mechanical w/o impact |
℃ | UL-746B | |
|
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ASTM D1525 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame Class Rating Flame Class Rating |
|||
|
1.5 mm 1.5 mm |
UL 94 | ||
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部 
美裂解装置寻求非化石能源
2021-05-11 搜料网资讯： Equale和MEGlobal公司前首席执行官表示，美国裂解装置最终将以氢气而非天然气作为主要能源，以显著降低碳足迹。 如果在美国使用的包装材料都至少含有30%的可回收成分， |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付