牌号简介 About |
---|
本材料为30%玻璃纤维增强,UL94 V-0/5V额定值。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.63 | g/cm³ | ASTM D792 |
特定体积 Specific volume Specific volume |
0.610 | cm³/g | ASTM D792 |
密度 Density Density |
1.63 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
250℃,5.0kg 250℃,5.0kg |
42 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate Melt Volume Rate |
|||
250℃,5 kg 250℃,5 kg |
29.0 | cm³/10min | ISO 1133 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
在拉伸杆上,MD On the stretching rod, MD |
% | 内部方法 | |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
在拉伸杆上,TD On the stretching rod, TD |
% | 内部方法 | |
TD:3.2 mm TD:3.2 mm |
% | 内部方法 | |
吸水率 Water Absorption Water Absorption |
|||
饱和 saturated,23℃ Saturated, 23 ℃ |
% | ISO 62 | |
平衡 equilibrium,23℃,50% RH Balanced Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
耐候性 Weather resistance Weather resistance |
UL 746C | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
ISO 180/1A | ||
23℃ 23℃ |
J/m | ASTM D4812 | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 unannealed,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火 unannealed,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火 unannealed,100 mm跨距 0.45 MPa, unannealed, 100 mm span |
℃ | ISO 75-2/Be | |
1.8 MPa,未退火 unannealed,100 mm跨距 1.8 MPa, unannealed, 100 mm span |
℃ | ISO 75-2/Ae | |
1.8 MPa,未退火 unannealed,64 mm跨距 1.8 MPa, unannealed, 64 mm span |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ASTM D1525 11 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball Pressure Test Ball Pressure Test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD TD |
ISO 11359-2 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ISO 11359-2 | |
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD MD |
ISO 11359-2 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ISO 11359-2 | |
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ISO 11359-2 | |
导热系数 Thermal Conductivity Thermal conductivity |
W/m/K | ISO 8302 | |
相对温度指数 Relative Temp Index(RTI) Relative Temperature Index (RTI) |
|||
电气性能 elec Electrical performance Elec |
℃ | UL 746 | |
强度机械性能 str Strength mechanical performance str |
℃ | UL 746 | |
冲击机械性能 imp Impact mechanical performance IMP |
℃ | UL 746 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface Resistivity Surface Resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | ASTM D257 | |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | IEC 60093 | |
介电强度 Dielectric Strength Dielectric Strength |
ASTM D149 | ||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
介电强度 Dielectric Strength Dielectric Strength |
IEC 60243-1 | ||
0.8 mm,在油中 0.8 mm in oil |
kV/mm | IEC 60243-1 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric Constant Dielectric Constant |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
相对电容率 Relative Permittivity Relative permittivity |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation Factor Dissipation Factor |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation Factor Dissipation Factor |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc Resistance Arc Resistance |
ASTM D495 | ||
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
UL 746 | ||
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
IEC 60112 | ||
CTI CTI |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High Voltage Arc Track Rate High Voltage Arc Track Rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot Wire Ignition Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 | ||
0.40 mm 0.40 mm |
UL 94 | ||
0.71 mm 0.71 mm |
UL 94 | ||
2.00 mm 2.00 mm |
UL 94 | ||
灼热丝可燃性指数GWFI Glow Wire Flammability Index GWFI |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Oxygen Index Oxygen Index |
% | ISO 4589-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ISO 527-1-2 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
断裂 brk Broken BRK |
MPa | ISO 527-2/5 | |
断裂 brk Broken BRK |
MPa | ASTM D638 | |
屈服 yld Yield yld |
MPa | ISO 527-2/5 | |
屈服 yld Yield yld |
MPa | ASTM D638 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk Broken BRK |
% | ISO 527-2/5 | |
断裂 brk Broken BRK |
% | ASTM D638 | |
屈服 yld Yield yld |
% | ISO 527-2/5 | |
屈服 yld Yield yld |
% | ASTM D638 | |
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ISO 178 | |
50 mm跨距 50 mm span |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
MPa | ISO 178 | |
断裂 brk,50 mm跨度 Broken BRK, 50 mm span |
MPa | ASTM D790 | |
泰伯耐磨性 Taber Abrasion Taber Abrasion |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | 内部方法 | |
洛氏硬度 Rockwell Hardness Rockwell hardness |
|||
R 级 R-level |
ISO 2039-2 | ||
R 级 R-level |
ASTM D785 | ||
球压硬度 ball-indentation hardness Ball indentation hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
人机交互的机器时代势不可挡
2021-09-20 搜料网资讯: 10月25日,2016世界机器人大会在京闭幕。在短短5天会期里,数万名热情观众蜂拥而至各大展馆,五花八门的各式机器人开始进入大众视野。一个人机交互的机器时代正裹挟 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |