| 牌号简介 About |
|---|
产品描述 Product Description
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
比重 Specific Gravity Specific Gravity |
1.41 | ASTM D792 | |
|
吸湿性 Moisture Absorption Moisture Absorption |
0.04 | % | ASTM D570 |
|
灰份含量 Ash Content Ash Content |
15 | % | 内部方法 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell Hardness Rockwell hardness |
90 | M | ASTM D-785 |
|
拉伸强度 Tensile Strength Tensile Strength |
900 | kg/cm² | ASTM D638 |
|
拉伸伸长率 Tensile Elongation Tensile Elongation |
% | ASTM D638 | |
|
弯曲强度 Flexural Strength Flexural Strength |
kg/cm² | ASTM D790 | |
|
弯曲模量 Flexural Modulus Flexural Modulus |
kg/cm² | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
kg-cm/cm | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT Hot deformation temperature HDT |
|||
|
1.80 MPa 1.80 MPa |
℃ | ASTM D648 | |
|
0.45 MPa 0.45 MPa |
℃ | ASTM D648 | |
|
熔融温度 Melting temperature Melting temperature |
℃ | 内部方法 | |
|
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
cm/cm/℃ | ASTM D696 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume Resistivity Volume Resistance |
ohm·cm | ASTM D257 | |
|
表面电阻率 Surface Resistivity Surface Resistivity |
ohm | ASTM D257 | |
|
绝缘强度 insulation Strength Insulation Strength |
kV/mm | ASTM D-149 | |
|
介电常数 Dielectric Constant Dielectric Constant |
ASTM D150 | ||
|
耗散因数 Dissipation Factor Dissipation Factor |
ASTM D150 | ||
|
耐电弧性 Arc Resistance Arc Resistance |
sec | ASTM D495 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame Class Rating Flame Class Rating |
|||
|
0.71 mm 0.71 mm |
calss | UL 94 | |
|
1.5 mm 1.5 mm |
calss | UL 94 | |
|
3.0 mm 3.0 mm |
calss | UL 94 | |
|
HWI HWI |
|||
|
0.71 mm 0.71 mm |
PLC | UL 746A | |
|
1.5 mm 1.5 mm |
PLC | UL 746A | |
|
3.0 mm 3.0 mm |
PLC | UL 746A | |
|
HAI HAI |
|||
|
0.71 mm 0.71 mm |
PLC | UL 746A | |
|
1.5 mm 1.5 mm |
PLC | UL 746A | |
|
3.0 mm 3.0 mm |
PLC | UL 746A | |
|
RTI RTI |
|||
|
ELEC ELEC |
|||
|
0.71 mm 0.71 mm |
℃ | UL 746B | |
|
1.5 mm 1.5 mm |
℃ | UL 746B | |
|
3.0 mm 3.0 mm |
℃ | UL 746B | |
|
IMP IMP |
|||
|
0.71 mm 0.71 mm |
℃ | UL 746B | |
|
1.5 mm 1.5 mm |
℃ | UL 746B | |
|
3.0 mm 3.0 mm |
℃ | UL 746B | |
|
STR STR |
|||
|
0.71 mm 0.71 mm |
℃ | UL 746B | |
|
1.5 mm 1.5 mm |
℃ | UL 746B | |
|
3.0 mm 3.0 mm |
℃ | UL 746B | |
|
CTI CTI |
PLC | IEC 60112 | |
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部
巴陵石化3月启动厂区内卸车站台优化改造
2018-11-23 巴陵石化炼油部苯乙烯装置2012年建成投产，苯乙烯产品主要内供并有部分外销。原产品充装站台在厂区外依山修建，经多年使用，出现地面鼓包、龙门架轻微移位等现象，存在山体滑坡隐患，而且站台充装产品类别单一，不利于出厂产品集中管理，采用敞开式装车设施也不能满足新的环保标准。 对此，该部今年3月启动厂区内装车站台优化改造，使之具备充装苯乙烯产品的条件。改造中，该部运用持续改进工具进行分析统筹，对改造过程全面把关。该部制定苯乙烯装车设施投用详细方案，严格检查苯乙烯产品的进料管线、储罐、 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付