牌号简介 About |
---|
本产品为40%玻纤增强聚酮改性材料,兼顾了高模量和强度,具有优秀的耐磨性,能快速成型。特别适用于高强度齿轮部件等结构。 |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 Tensile Strength Tensile Strength |
|||
屈服 yld Yield yld |
165 | MPa | ASTM D638 |
屈服 yld Yield yld |
165 | MPa | ISO 527-2 |
断裂伸长率 Elongation at Break Elongation at Break |
|||
|
2.9 | % | ASTM D638 |
|
2.9 | % | ISO 527-1 |
弯曲强度 Flexural Strength Flexural Strength |
|||
|
220 | MPa | ASTM D790 |
|
MPa | ISO 178 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
|
MPa | ASTM D790 | |
|
MPa | ISO 178 | |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
|
MPa | ASTM D638 | |
|
MPa | ISO 527 | |
洛氏硬度 Rockwell Hardness Rockwell hardness |
R | ASTM D-785 | |
邵氏硬度 Shore hardness Shore hardness |
Shore D | ISO 868 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
KJ/m² | ISO 180/1A | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
比重 Specific Gravity Specific Gravity |
|||
|
ASTM D792 | ||
|
ISO 1183 | ||
熔体体积流动速率 Melt Volume Rate Melt Volume Rate |
|||
240℃,2.16kg 240℃,2.16kg |
cm³/10min | ISO 1133 | |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
240℃,2.16kg 240℃,2.16kg |
g/10min | ASTM D1238 | |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
纵向 flow Vertical flow |
% | ASTM D955 | |
横向 across flow Horizontal Across Flow |
% | ASTM D955 | |
吸水率 Water Absorption Water Absorption |
|||
|
% | ASTM D570 | |
|
% | ISO 62 | |
吸湿性 Moisture Absorption Moisture Absorption |
|||
|
% | ISO 62 | |
|
% | ASTM D570 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
0.45 MPa 0.45 MPa |
℃ | ASTM D648 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/-2 | |
1.8 MPa 1.8 MPa |
℃ | ASTM D648 | |
1.8 MPa 1.8 MPa |
℃ | ISO 75-1/-2 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
|||
|
℃ | ASTM D1525 | |
|
℃ | ISO 306/B | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
纵向 flow Vertical flow |
×10-6/℃ | ASTM E831 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
ohm·cm | ASTM D257 | |
表面电阻率 Surface Resistivity Surface Resistivity |
ohm | ASTM D257 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
60Hz 60Hz |
ASTM D150 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
60Hz 60Hz |
E-4 | ASTM D150 | |
绝缘强度 insulation Strength Insulation Strength |
|||
|
kV/mm | ASTM D-149 | |
|
kV/mm | ASTM D-149 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
新一轮数字化制造浪潮推进3D打印行业开展
2016-06-21 当前全球正在兴起新一轮数字化制造浪潮,发达国家为应对制造业竞争力的下降,大力倡导“再工业化、再制造化”,抓手就是3D打印等先进制造技术。3D打印为代表的先进制造成为各国政府抢占的战略高地。 3D打印技术从单纯的技术创新成为颠覆传统生产制造方式的新生力量。然而,从传统的中心式生产到分散式生产方式的转变,是更加深远的影响。 当前,3D打印技术正处于发展的井喷期,3D打印的数据标准可能影响到装备和应用两个方面,对此我们应该抓紧标准的研究,掌握话语权。 < |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |