牌号简介 About |
---|
POKETONE Polymer M93AG8H是一种40%短玻璃纤维增强的高级高流量注塑等级,其机械性能将其归类为工程热塑性塑料。该牌号表现出韧性和高模量的独特平衡,同时具有良好的蠕变性能、强度和高温性能。 |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 Tensile Strength Tensile Strength |
|||
屈服 yld Yield yld |
165 | MPa | ASTM D638 |
屈服 yld Yield yld |
165 | MPa | ISO 527-2 |
断裂伸长率 Elongation at Break Elongation at Break |
|||
|
2.9 | % | ASTM D638 |
|
2.9 | % | ISO 527-1 |
弯曲强度 Flexural Strength Flexural Strength |
|||
|
220 | MPa | ASTM D790 |
|
MPa | ISO 178 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
|
MPa | ASTM D790 | |
|
MPa | ISO 178 | |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
|
MPa | ASTM D638 | |
|
MPa | ISO 527 | |
洛氏硬度 Rockwell Hardness Rockwell hardness |
R | ASTM D-785 | |
邵氏硬度 Shore hardness Shore hardness |
Shore D | ISO 868 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
KJ/m² | ISO 180/1A | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
比重 Specific Gravity Specific Gravity |
|||
|
ASTM D792 | ||
|
ISO 1183 | ||
熔体体积流动速率 Melt Volume Rate Melt Volume Rate |
|||
240℃,2.16kg 240℃,2.16kg |
cm³/10min | ISO 1133 | |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
240℃,2.16kg 240℃,2.16kg |
g/10min | ASTM D1238 | |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
纵向 flow Vertical flow |
% | ASTM D955 | |
横向 across flow Horizontal Across Flow |
% | ASTM D955 | |
吸水率 Water Absorption Water Absorption |
|||
|
% | ASTM D570 | |
|
% | ISO 62 | |
吸湿性 Moisture Absorption Moisture Absorption |
|||
|
% | ISO 62 | |
|
% | ASTM D570 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
0.45 MPa 0.45 MPa |
℃ | ASTM D648 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/-2 | |
1.8 MPa 1.8 MPa |
℃ | ASTM D648 | |
1.8 MPa 1.8 MPa |
℃ | ISO 75-1/-2 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
|||
|
℃ | ASTM D1525 | |
|
℃ | ISO 306/B | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
纵向 flow Vertical flow |
×10-6/℃ | ASTM E831 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
ohm·cm | ASTM D257 | |
表面电阻率 Surface Resistivity Surface Resistivity |
ohm | ASTM D257 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
60Hz 60Hz |
ASTM D150 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
60Hz 60Hz |
E-4 | ASTM D150 | |
绝缘强度 insulation Strength Insulation Strength |
|||
|
kV/mm | ASTM D-149 | |
|
kV/mm | ASTM D-149 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
【万华化学新里程碑】百万吨乙烯项目开始全面投产
2020-11-11 搜料网资讯: 作为2020年的中国500强之一,山东烟台的万华化学可以说是山东人民的骄傲了,他同时也是山东省范围内第一家先改制后上市的股份制公司,拥有着庞大的员工团体和投资巨 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |