公司信息及水印
牌号简介 About |
---|
Texin 990AR树脂是一种以聚醚为基础的热塑性聚氨酯,肖氏硬度约为90A,含有一种内释型添加剂。这种树脂可以通过注塑或挤出加工。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ASTM D792 |
密度 Density |
1.13 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:2.54 mm TD:2.54 mm |
0.80 | % | ASTM D955 |
MD:2.54 mm MD:2.54 mm |
0.80 | % | ASTM D955 |
TD:2.54 mm TD:2.54 mm |
0.80 | % | ISO 2577 |
MD:2.54 mm MD:2.54 mm |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 A Shaw's A |
ISO 868 | ||
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ISO 4649 | |
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D1044 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D412 | |
屈服 yield |
MPa | ISO 37 | |
300% 应变 300% strain |
MPa | ISO 37 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
100% 应变 100% strain |
MPa | ISO 37 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
50% 应变 50% strain |
MPa | ISO 37 | |
50% 应变 50% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 37 | |
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
撕裂强度 tear strength |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 974 | |
玻璃化转变温度 Glass transition temperature |
℃ | DMA | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/50 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ASTM D573 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 | |
100% Strain,100℃,70 hr 100% Strain,100℃,70 hr |
% | ASTM D573 | |
300% Strain,100℃,70 hr 300% Strain,100℃,70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100% Strain,100℃,168 hr 100% Strain,100℃,168 hr |
% | ASTM D573 | |
300% Strain,100℃,168 hr 300% Strain,100℃,168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 | |
100% Strain,100℃,336 hr 100% Strain,100℃,336 hr |
% | ASTM D573 | |
300% Strain,100℃,336 hr 300% Strain,100℃,336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 | |
100% Strain,100℃,504 hr 100% Strain,100℃,504 hr |
% | ASTM D573 | |
300% Strain,100℃,504 hr 300% Strain,100℃,504 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ISO 216 | |
100% Strain 100℃,70 hr 100% Strain 100℃,70 hr |
% | ISO 216 | |
300% Strain 100℃,70 hr 300% Strain 100℃,70 hr |
% | ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ISO 216 | |
100% Strain 100℃,168 hr 100% Strain 100℃,168 hr |
% | ISO 216 | |
300% Strain 100℃,168 hr 300% Strain 100℃,168 hr |
% | ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ISO 216 | |
100% Strain 100℃,336 hr 100% Strain 100℃,336 hr |
% | ISO 216 | |
300% Strain 100℃,336 hr 300% Strain 100℃,336 hr |
% | ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ISO 216 | |
100% Strain 100℃,504 hr 100% Strain 100℃,504 hr |
% | ISO 216 | |
300% Strain 100℃,504 hr 300% Strain 100℃,504 hr |
% | ISO 216 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ISO 216 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 D,100℃,70 hr Shore D, 100 ℃, 70 hr |
ASTM D573 | ||
邵氏 D,100℃,168 hr Shore D, 100 ℃, 168 hr |
ASTM D573 | ||
邵氏 D,100℃,336 hr Shore D, 100 ℃, 336 hr |
ASTM D573 | ||
邵氏 D,100℃,504 hr Shore D, 100 ℃, 504 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 216 | ||
邵氏 D,100℃,70 hr Shore D, 100 ℃, 70 hr |
ISO 216 | ||
邵氏 D,100℃,168 hr Shore D, 100 ℃, 168 hr |
ISO 216 | ||
邵氏 D,100℃,336 hr Shore D, 100 ℃, 336 hr |
ISO 216 | ||
邵氏 D,100℃,504 hr Shore D, 100 ℃, 504 hr |
ISO 216 | ||
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain,23℃,70 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain,23℃,70 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain,23℃,168 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain,23℃,168 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain,23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain,23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain,23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain,23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
拉伸强度的变化率 The rate of change in tensile strength |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain,23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain,23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain,23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain,23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain,23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain,23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain,23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain,23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
邵氏硬度的变化率 The rate of change in Shore hardness |
ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料C中 |
ASTM D471 | ||
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23 ℃, 168 hr, in reference fuel |
ASTM D471 | ||
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23 ℃, 336 hr, in reference fuel C |
ASTM D471 | ||
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23 ℃, 504 hr, in reference fuel C |
ASTM D471 | ||
邵氏 D,100℃,70 hr,在ASTM #1油中 |
ASTM D471 | ||
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,168 hr,在ASTM #1油中 |
ASTM D471 | ||
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100 ℃, 168 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100 ℃, 336 hr, in ASTM # 1 oil |
ASTM D471 | ||
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100 ℃, 336 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100 ℃, 504 hr, in ASTM # 1 oil |
ASTM D471 | ||
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100 ℃, 504 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料C中 |
ISO 175 | ||
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23 ℃, 168 hr, in reference fuel |
ISO 175 | ||
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23 ℃, 336 hr, in reference fuel C |
ISO 175 | ||
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23 ℃, 504 hr, in reference fuel C |
ISO 175 | ||
邵氏 D,100℃,70 hr,在ASTM #1油中 |
ISO 175 | ||
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100 ℃, 70 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,168 hr,在ASTM #1油中 |
ISO 175 | ||
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100 ℃, 168 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100 ℃, 336 hr, in ASTM # 1 oil |
ISO 175 | ||
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100 ℃, 336 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100 ℃, 504 hr, in ASTM # 1 oil |
ISO 175 | ||
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100 ℃, 504 hr, in ASTM # 3 oil |
ISO 175 | ||
体积变化 Volume change |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A 23℃,70 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A 23℃,168 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A 23℃,336 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A 23℃,504 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
体积变化 Volume change |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A 23℃,70 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A 23℃,168 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A 23℃,336 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A 23℃,504 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩载荷 Compression load |
ASTM D575 | ||
10% 挠曲 10% deflection |
MPa | ASTM D575 | |
15% 挠曲 15% deflection |
MPa | ASTM D575 | |
2% 挠曲 2% deflection |
MPa | ASTM D575 | |
20% 挠曲 20% deflection |
MPa | ASTM D575 | |
25% 挠曲 25% deflection |
MPa | ASTM D575 | |
5% 挠曲 5% deflection |
MPa | ASTM D575 | |
50% 挠曲 50% deflection |
MPa | ASTM D575 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 Post-cured 16 hr at 230°F |
4 速率 A (50°C/h) |
【新闻资讯】查看全部
SABIC推出中国市场定制处置方案
2016-05-06 在刚刚结束的2016年国际橡塑展(CHINAPLAS)上,SABIC针对中国快速城市化进程中出现的各种问题,推出创新可持续的材料解决方案,提高人们生活水平并改善环境质量。 从“中国制造”到“中国创造” SABIC关注的重点领域之一是设计开发下一代技术,提升科学价值并帮助客户实现商业抱负,这与中国“十三五”规划提出的致力于创新驱动发展并推动产业向价值链上游进军的理念不谋而合。 为满足中国市场的特定需求,SABIC与整个价值链上的产业利益相关者进 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |