牌号简介 About |
---|
PA 6,30%玻璃纤维,注射成型,无卤阻燃 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.423 | g/cm³ | ISO 1183 |
模具收缩率 Mold Shrinkage Mold Shrinkage |
|||
TD:270℃,2.0 mm TD:270℃,2.0 mm |
0.70 | % | ISO 294-4 |
MD:270℃,2.0 mm MD:270℃,2.0 mm |
0.20 | % | ISO 294-4 |
后期收缩 Post shrinkage Post shrinkage |
|||
TD:120℃,2.0 mm TD:120℃,2.0 mm |
0.10 | % | ISO 294-4 |
MD:120℃,2.0 mm MD:120℃,2.0 mm |
0.10 | % | ISO 294-4 |
吸水率 Water Absorption Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁冲击强度 Charpy Impact strength Charpy Impact strength of simply supported beams |
|||
23℃ 23℃ |
KJ/m² | ISO 179-1eU | |
-30℃ -30℃ |
KJ/m² | ISO 179-1eU | |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁冲击强度 Izod Impact strength Izod Impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1U | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
KJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature Melting temperature |
|||
10 °C/min 10 °C/min |
℃ | ISO 11357-1,-3 | |
热变形温度 HDT Hot deformation temperature HDT |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-1,-2 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-1,-2 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
|||
50 N; 120 °C/h 50 N; 120 °C/h |
℃ | ISO 306 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
×10-4/K | ISO 11359-1,-2 | |
TD:23~55℃ TD:23~55℃ |
×10-4/K | ISO 11359-1,-2 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric Constant Dielectric Constant |
|||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
体积电阻率 Volume Resistivity Volume Resistance |
ohm·m | IEC 60093 | |
介电强度 Dielectric Strength Dielectric Strength |
|||
1 mm 1 mm |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
UL阻燃等级 UL flame retardant rating |
|||
1.50mm 1.50mm |
class | UL 94 | |
0.75mm 0.75mm |
class | UL 94 | |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
1.5mm 1.5mm |
class | UL 94 | |
氧指数 Oxygen Index Oxygen Index |
|||
解决方案 A Solution A |
% | ISO 4589-2 | |
灼热丝可燃性指数GWFI Glow Wire Flammability Index GWFI |
|||
0.40 mm 0.40 mm |
℃ | IEC 60695-2-12 | |
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Glow Wire Ignitability Temperature(GWIT) Glow Wire Ignitability Temperature (GWIT) |
|||
0.4 mm 0.4 mm |
℃ | IEC 60695-2-13 | |
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
1 mm/min 1 mm/min |
MPa | ISO 527-1,-2 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
5 mm/min,断裂 5 mm/min, fracture |
MPa | ISO 527-1,-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
5 mm/min,断裂 5 mm/min, fracture |
% | ISO 527-1,-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
2 mm/min 2 mm/min |
MPa | ISO 178-A | |
弯曲强度 Flexural Strength Flexural Strength |
|||
2 mm/min 2 mm/min |
MPa | ISO 178-A | |
弯曲应变 Flexural Strain Flexural Strain |
|||
2 mm/min 2 mm/min |
% | ISO 178-A |
备注 |
---|
2. 60x60x2mm, 4 hr |
3. 60x60x2mm, 80°C MT, 600 bar |
4. 2.0 mm/min |
5. 2 mm/min |
6. 10°C/min |
7. Solution A |
8. 程序 A |
【新闻资讯】查看全部
负责人被追刑责,山东鼎鼎化学“10·26” 爆炸事故调查报告发布
2022-02-20 2021年10月26日5时31分,位于淄博市高青县经济开发区的山东鼎鼎化学科技股份有限公司(以下简称鼎鼎公司)发生一起爆炸事故,造成1人受伤,直接损失约342万元。 近日,山东淄博应急 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |