牌号简介 About |
---|
Adiprene LFG 740D是一种TDI端接的聚醚预聚物,当用4,4’-亚甲基双(邻氯苯胺)MBCA固化时,得到75邵尔D弹性体。ADIPRENE LFG 740D的特点包括:低游离TDI含量(低于0.1%),良好的高温动力学,低粘度LFG 740D由于游离TDI含量低(低于0.1%),在处理和加工过程中比传统型预聚物提供了更高的安全性。 ADIPRENE LFG 740D is a TDI-terminated polyether prepolymer that, when cured with 4,4'-methylene-bis-(o-chloroaniline),MBCA, yields a 75 Shore D elastomer. The features of ADIPRENE LFG 740D include: Low Free TDI Content (below 0.1%) Good High Temperature Dynamics Low Viscosity LFG 740D offers improved safety during handling and processing over conventional-type prepolymers due to the low content of free TDI, less than 0.1%. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.24 | g/cm³ | ASTM D792 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
裤型撕裂耐性 Pant tear resistance |
56.0 | N/mm | ASTM D1938 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变 100% strain |
26.2 | MPa | ASTM D412 |
300% 应变 300% strain |
37.9 | MPa | ASTM D412 |
拉伸强度 tensile strength |
41.4 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
-- -- 2 |
kN/m | ASTM D624 | |
开裂 cracking |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
储存稳定性 storage stability |
min | ||
脱模时间 stripping time |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
动态特性 Dynamic characteristics |
|||
动态模量:30℃ Dynamic modulus: 30 ℃ |
dynes/cm² | ||
动态模量:50℃ Dynamic modulus: 50 ℃ |
dynes/cm² | ||
动态模量:70℃ Dynamic modulus: 70 ℃ |
dynes/cm² | ||
动态模量:130℃ Dynamic modulus: 130 ℃ |
dynes/cm² | ||
动态模量:150℃ Dynamic modulus: 150 ℃ |
dynes/cm² | ||
正切:30℃ Tangent: 30 ℃ |
|||
正切:50℃ Tangent: 50 ℃ |
|||
正切:70℃ Tangent: 70 ℃ |
|||
正切:130℃ Tangent: 130 ℃ |
|||
正切:150℃ Tangent: 150 ℃ |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
100℃ 100℃ |
hr | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
压缩强度 compressive strength |
ASTM D695 | ||
5% 应变 5% strain |
MPa | ASTM D695 | |
10% 应变 10% strain |
MPa | ASTM D695 | |
15% 应变 15% strain |
MPa | ASTM D695 | |
20% 应变 20% strain |
MPa | ASTM D695 | |
25% 应变 25% strain |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
海南炼化工程建立发动会在海南炼化召开
2019-01-03 2018年12月28日,海南炼化100万吨/年乙烯及炼油改扩建工程建设动员会在海南炼化召开,标志着该项目主体工程正式开工。 海南炼化100万吨/年乙烯及炼油改扩建工程是列入国家石化产业规划的重点项目,更是中国石化推进“两个三年、两个十年”战略部署,打造世界一流能源化工公司的支撑项目。项目投产后,将很大程度促进先进农业、绿色化工、旅游健康等下游产业发展,提高中国石化国际市场竞争力,保障国家能源安全,带动海南省经济发展和助力海南自贸区(港)建设。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |