| 牌号简介 About |
|---|
| 对于工业和消费类薄膜应用，极高的冲击强度、低阻塞倾向、改善的处理和可兑换性符合：美国FDA 21 CFR 177.1520（c）3.2a。加拿大HPFB无异议，请参考法规了解完整细节。ELITE™ 5100G增强聚乙烯树脂是由陶氏塑料通过InSite技术生产的共聚物。它具有优异的冲击强度、良好的拉伸和穿孔性能，适用于厚、薄规格工业和消费吹塑薄膜应用。这种树脂表现出比LLDPE更高的热粘强度，使其成为自动化包装应用的理想选择。 For industrial and consumer film applications Extremely high impact strength Low blocking tendencies for improved handling and convertibility Complies with: U.S. FDA 21 CFR 177.1520 (c) 3.2a. Canadian HPFB No Objection Consult the regulations for complete details. ELITE™ 5100G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow Plastics. It offers excellent impact strength, good tensile and puncture properties for thick and thin gauge industrial and consumer blown film applications. This resin exhibits higher hot tack strengths than LLDPE, making it ideal for automated packaging applications. |
产品描述 Product Description
加工条件：吹塑薄膜
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.920 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.85 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
25 | µm | |
|
膜刺穿强度 Membrane puncture strength |
5.76 | J | 内部方法 |
|
膜刺穿力 Membrane puncture force |
64.5 | N | 内部方法 |
|
膜耐刺穿性 Membrane puncture resistance |
J/cm³ | 内部方法 | |
|
膜强度 Membrane strength |
ASTM D882 | ||
|
MD MD |
J/cm³ | ASTM D882 | |
|
TD TD |
J/cm³ | ASTM D882 | |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD 1% secant, MD |
MPa | ASTM D882 | |
|
2% 正割，MD 2% secant, MD |
MPa | ASTM D882 | |
|
1% 正割，TD 1% secant, TD |
MPa | ASTM D882 | |
|
2% 正割，TD 2% secant, TD |
MPa | ASTM D882 | |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服 MD, yield |
MPa | ASTM D882 | |
|
TD，屈服 TD, yield |
MPa | ASTM D882 | |
|
MD，断裂 MD, fracture |
MPa | ASTM D882 | |
|
TD，断裂 TD, fracture |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂 MD, fracture |
% | ASTM D882 | |
|
TD，断裂 TD, fracture |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD MD |
g | ASTM D1922 | |
|
TD TD |
g | ASTM D1922 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45° 45° |
ASTM D2457 | ||
|
雾度 Haze |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
PPG和Aerobrand宣布建立飞机涂层设计合作关系
2022-07-19 最近，PPG宣布将与英国航空公司品牌和设计咨询公司Aerobrand合作，为航空公司客户提供独特的服务，将油漆供应与涂料设计相结合。该合作关系将使客户能够与设计师密切合作，创造定 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付