牌号简介 About |
---|
SQ185 UVFR SiO NC001是一种紫外线稳定的高流动性不透明注塑(IM)级的聚碳酸酯(PC)硅氧烷共聚物树脂。该树脂提供基于非溴、非氯FR系统的UL94 V0@1.5毫米阻燃性、极低温延展性(-40摄氏度)特性和极好的加工性,与标准PC相比,IM循环时间更短。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.19 | g/cm³ | ASTM D792 |
密度 Density Density |
1.19 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
16 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
15.1 | cm³/10min | ISO 1133 |
收缩率 Shrinkage Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.40 to 0.80 | % | 内部方法 |
吸水率 Water Absorption Water Absorption |
|||
饱和 saturated,23℃ Saturated, 23 ℃ |
% | ISO 62 | |
平衡 equilibrium,23℃,50% RH Balanced Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
耐候性 Weather resistance Weather resistance |
UL 746C | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ISO 527-1-2 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
断裂 brk Broken BRK |
MPa | ISO 527-2/50 | |
断裂 brk Broken BRK |
MPa | ASTM D638 | |
屈服 yld Yield yld |
MPa | ISO 527-2/50 | |
屈服 yld Yield yld |
MPa | ASTM D638 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk Broken BRK |
% | ASTM D638 | |
断裂 brk Broken BRK |
% | ISO 527-2/50 | |
屈服 yld Yield yld |
% | ISO 527-2/50 | |
屈服 yld Yield yld |
% | ASTM D638 | |
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ISO 178 | |
50 mm 50 mm |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
屈服 yld,50 mm Yield yld, 50 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 unannealed,64 mm跨距 1.8 MPa, unannealed, 64 mm span |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火 unannealed,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative Temp Index(RTI) Relative Temperature Index (RTI) |
|||
电气性能 elec Electrical performance Elec |
℃ | UL 746 | |
强度机械性能 str Strength mechanical performance str |
℃ | UL 746 | |
冲击机械性能 Imp Impact mechanical performance Imp |
℃ | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数GWFI Glow Wire Flammability Index GWFI |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Glow Wire Ignitability Temperature(GWIT) Glow Wire Ignitability Temperature (GWIT) |
IEC 60695-2-13 | ||
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
开拓生物降解高分子材料、推动绿色环保生活的践行者---卡帝德
2020-09-23 搜料网资讯: 为了杜绝塑料造成的白色污染,响应国家治理塑料污染的号召,卡帝德塑化科技有限公司全力推出了全生物降解改性材料,生产生物可降解塑料,有效提高塑料降解速度, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |