APEL™ APL6013T是一种环烯烃共聚物 (COC)材料,。 该产品在北美洲有供货,。 APEL™ APL6013T的典型应用领域为:瓶子。 APEL™ APL6013T APEL™ APL6013T is a Cyclic Olefin Copolymer (COC) material. It is available in North America. Typical application of APEL™ APL6013T: Bottles APEL™ APL6013T APEL is a cyclo olefin copolymer (COC) developed by Mitsui Chemicals using Ziegler polymerization technology. Integration of the performance of polyolefin resins and that of amorphous resins enables control of heat resistance and fluidity. With the highest refractive index among amorphous polyolefins, it is low in optical anisotropy and extremely low in birefringence. Proven applications in optical plastic lenses. Excellent moisture-proof properties, chemical resistance and non-attachment characteristics that make it applicable as a medical packaging material. APEL's versatile functions and superior characteristics create new potential for transparent materials. Features: Optical characteristics Moisture-proofness Chemical resistance Dimensional stability Heat resistant stiffness Superior moldability Applications: Industrial parts |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,2.16kg 260℃,2.16kg |
15 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.60 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
60.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
3.0 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
水气透过率 Water vapor transmittance |
g·mm/m²/atm/24 hr | ASTM F1249 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
可折叠塑料快递盒 反复运用中降低快递净化
2017-10-24 “双十一”逼近,网友在陷入买买买的热潮中的时候,一些环保人士也在关注一个问题,即快递包装污染。 国家邮政局统计数据显示:2016年中国快递业务量首次突破312亿件,相当于年人均快递使用量近23件。2015年中国消耗了99.22亿个包装箱、169.85亿米胶带以及82.68亿个塑料袋。其中胶带的长度可绕地球赤道425圈。如果按照每个包装箱0.2公斤估算,这些快递就会产生包装垃圾400多万吨。 你还记得收到多少快递盒不?如果不用纸盒子,你觉得哪种材质的快递盒子更 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |