牌号简介 About |
---|
HEPLA®H9040GF是一种40%玻璃纤维增强聚邻苯二甲酰胺(PPA),具有高硬度和强度,以及耐高温和耐化学性。即使在高机械负荷下,应用也是具有严格尺寸公差的零件。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
23℃ 23℃ |
1.5 | g/cm³ | ISO 1183 |
Spiral Flow 1,2 Spiral Flow 1,2 |
30 | cm | NFD Method |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
0.8 | % | |
MD MD |
0.2 | % | |
Humidity Absorption - 62% RH (70℃) Humidity Absorption - 62% RH (70℃) |
% | ISO 1110 | |
Hardness Hardness |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Ball Indentation Hardness (H 961/30) Ball Indentation Hardness (H 961/30) |
MPa | ISO 2039-1 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1 | |
Tensile Stress (Break) Tensile Stress (Break) |
MPa | ISO 527-2/5 | |
Tensile Strain (Break) Tensile Strain (Break) |
% | ISO 527-2/5 | |
Flexural Modulus 3 Flexural Modulus 3 |
MPa | ISO 178 | |
Flexural Stress 3 Flexural Stress 3 |
MPa | ISO 178 | |
Flexural Strain at Break 4 Flexural Strain at Break 4 |
% | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
600 600 |
IEC 60112 | ||
Solution A Solution A |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa, Unannealed 8.0 MPa, Unannealed |
℃ | ISO 75-2/C | |
Melting Temperature 5 Melting Temperature 5 |
℃ | DIN EN 11357-1 | |
Temperature Index Temperature Index |
|||
50% Loss of Tensile Strength 50% Loss of Tensile Strength |
|||
20000 hr 20000 hr |
|||
50% Loss of Tensile Strength 50% Loss of Tensile Strength |
|||
5000 hr 5000 hr |
|||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Burning Rate 6 (1.00 mm) Burning Rate 6 (1.00 mm) |
mm/min | FMVSS 302 | |
阻燃等级 Flame retardant level |
|||
0.8 mm 0.8 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
960 960 |
IEC 60695-2-12 | ||
1.6 mm 1.6 mm |
|||
Additional Information Additional Information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Reinforcement Content Reinforcement Content |
% | ISO 1172 |
备注 |
---|
1 Mold Temperature: 130℃, Melt Temperature: 340℃, Injection Pressure: 750 bar |
【新闻资讯】查看全部
艾曼斯Grivory GV链轮-完满的以塑代钢
2020-08-28 艾曼斯Grivory GV半芳香族尼龙天生具有良好的机械性能(尺寸稳定性,拉伸模量轻松达到18000MPa以上),优异的耐蠕变和耐化、耐候性。 在此基础上改性的材料用在链轮上,跟通常使用的塑钢链轮相 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |