牌号简介 About |
---|
Noryl SE100x树脂PPE+PS混合物。未填充的无溴、无氯FR系统。UL94 v0/v1额定。RTI电子/IMP/STR 95/80/95。良好的流动性。适用于E/E市场室内/室外应用。Noryl SE100x树脂无溴、无氯FR树脂。提高了生产效率和可靠性。1990年HDT。 PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/V1 rated. RTI Elec/Imp/Str 95/80/95. Good flow. Suitable for E/E market indoor/outdoor applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.10 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
TD TD 2 |
0.50 to 0.70 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
0.50 to 0.70 | % | 内部方法 |
耐候性 Weathering resistance |
f1 | UL 746C | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
断裂 fracture 3 |
46.9 | MPa | ASTM D638 |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
100 mm跨距 100 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
屈服,100 mm跨度 Yield, 100 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-30℃,Energy at Peak Load -30℃,Energy at Peak Load |
J | ASTM D3763 | |
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance 5 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
6.00 mm 6.00 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
辐射板 Listing(UL) Radiation Plate Listing (UL) |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 类型 1, 2.0 in/min |
4 0.10 in/min |
5 钨电极 |
【新闻资讯】查看全部
德国公司试飞电动空中出租车 计划2024年投入运行
2021-06-23 搜料网资讯: 据路透社报道,德国初创企业沃洛科普特公司21日在法国首次试飞公司生产的电动空中出租车,并表示计划在2024年巴黎奥运会期间将飞的投入运行。 报道称,这架电动飞行 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |