牌号简介 About |
---|
Polytrope Str 2030Reu是一种阻燃TPO树脂,符合UL 94 V-0和5VA标准,符合RoHS标准,专门为挤压和热成型工艺提供高熔融强度。它是不开花的,并提供平衡的抗冲击性和刚度,使它特别适用于面板和封闭应用需要阻燃性能。它可以在光滑或纹理表面挤压,或与增强聚烯烃帽树脂共同挤压,以进一步定制其耐用性,外观,或内部和外部应用的感觉。Polytrope Str 2030Reu在挤出和热成型过程中提供非常光滑的表面的能力使其非常适合用装饰膜层压工艺。它也很容易上色,可通过标准TPO油漆系统进行喷漆。 POLYTROPE STR 2030REU is a flame retardant TPO resin which is UL 94 V-0 and 5VA compliant, RoHS compliant, and specifically designed to provide high melt strength for extrusion, and thermoforming processes. It is non-blooming, and provides balanced impact resistance with stiffness, making it especially suitable for panel and closure applications requiring flame retarding properties. It can be extruded in smooth or textured surfaces, or co-extruded with a POLYTROPE STR enhanced polyolefin cap resin to further customize its' durability, appearance, or feel for interior and exterior applications. The capability of POLYTROPE STR 2030REU to provide an exceptionally smooth surface in extrusion and thermoforming makes it well suited to lamination processes with decorative films. It is also easily colored and is paintable by standard TPO paint systems. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.31 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
0.80 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
23℃,3.2 mm,24 hrs 23℃,3.2 mm,24 hrs |
0.80 到 1.2 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
19.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂,233℃ Fracture, 233 ℃ |
430 | % | ISO 527-2 |
弯曲模量 Bending modulus |
|||
弦,23℃ String, 23 ℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
流量,-30℃,3.2mm,注塑成型 Flow rate, -30 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
流量,23℃,3.2mm,注塑成型 Flow rate, 23 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
-9℃,Total Energy,韧性破坏 -9 ℃, Total Energy, toughness failure |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~100℃ MD:-30~100℃ |
1/℃ | ASTM E831 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
3.20 mm,所有颜色 3.20 mm, all colors |
UL 94 | ||
1.60 mm,所有颜色 1.60 mm, all colors |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,3180 µm,热塑,光滑 60 °, 3180 µ m, thermoplastic, smooth |
ISO 2813 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Sag(8 inch span,two point support,149℃,3.20 mm) Heat Sag(8 inch span,two point support,149℃,3.20 mm) |
mm | ASTM D3769 |
备注 |
---|
1 In process |
2 一般属性:这些不能被视为规格。 |
3 方法 A |
4 类型 1, 2.0 in/min |
5 类型1A, 0.079 in/min |
【新闻资讯】查看全部
巴陵石化依法维护合法权益两案胜诉
2016-09-05 8月23日,巴陵石化收到湖南岳阳市中级人民法院下达的民事裁定书,依法驳回一酒家业主要求该公司赔偿房屋损害20万元的再审请求。这起历时4年的诉讼案件巴陵石化胜诉。此前的7月,该公司经司法程序,将一处长达10余年的某出租场地依法收回,维护了合法权益。 巴陵石化法律事务部负责人介绍,2013年8月,该公司周边一酒家业主向法院提供房屋《司法鉴定意见》等证据材料,起诉巴陵石化在 1996年、1998年两次大洪水期间,因排水不及时使其酒家房屋被洪水浸泡,2002年又因施工造成其房屋损害 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |