| 牌号简介 About |
|---|
| Amodel AS -1133 HS是33％玻纤增强热稳定型聚邻苯二甲酰胺（PPA）树脂，即使是那些壁厚大于0.125英寸（ 3毫米）的成型部件，也具有优异的结构完整性 。 该结构性树脂的主要特性包括高热变形温度、高挠曲模量、高拉伸强度、优良的耐蠕变性和低吸湿性。 -黑色： AS-1145 HS BK 324 -本色： AS-1145 HS NT Amodel® AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.125 inch (3 mm). Key properties of this structural resin are high heat deflection temperature, high flexural modulus, high tensile strength, excellent creep resistance, and low moisture absorption. Black: AS-1145 HS BK 324 Natural: AS-1145 HS NT |
产品描述 Product Description
用途：机器/机械部件;连接器;动力/其它工具;金属取代;燃料管线;外壳;阀门/阀门部件;草坪和园林设备;厚壁配件（部件）;汽车领域的应用;工业应用;通用;工业部件;汽车电子;汽车的发动机罩下的零件;
颜色：自然色,黑色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 低吸湿性; 机械强度好; 热稳定性好; 尺寸稳定性好; 耐化学性; 耐高温; 韧性好; Good Rigidity,Good flexibility,Good Dimensional Stability,High Heat Resistance,Solvent resistance,Low moisture absorption,Heat Stabilized,HB
填料：玻璃纤维 45
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.56 | g/cm³ | ISO 1183/A |
|
收缩率 Shrinkage rate |
|||
|
TD TD |
0.60 | % | ASTM D955 |
|
MD MD |
0.20 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
0.12 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
12 | kJ/m² | ISO 179-1eA |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火，3.18 mm 1.8 MPa, annealed, 3.18 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，退火，3.2 mm 0.45 MPa, annealed, 3.2 mm |
℃ | ASTM D648 | |
|
连续使用温度 Continuous use temperature |
ASTM D3045 | ||
|
-- -- 2 |
℃ | ASTM D3045 | |
|
-- -- 3 |
℃ | ASTM D3045 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
ASTM E831 | ||
|
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
|
160 到 249℃ 160 to 249 ℃ |
cm/cm/℃ | ASTM E831 | |
|
MD MD |
ASTM E831 | ||
|
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
|
160 到 249℃ 160 to 249 ℃ |
cm/cm/℃ | ASTM E831 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level 4 |
|||
|
3.20 mm 3.20 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2 | |
|
断裂 fracture |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2 | |
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
屈服 yield |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
MPa | ASTM D732 | |
|
泊松比 Poisson's ratio |
ASTM E132 | ||
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 20000小时 |
| 3 5000小时 |
| 4 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
|
【新闻资讯】查看全部 
石大胜华投建硅基负极项目
2022-05-10 5月4日，山东石大胜华化工集团股份有限公司发布公告称，公司拟与员工持股平台东营盈嘉合壹产业投资合伙企业(有限合伙)设立合资子公司胜华新材料科技(眉山)有限公司，投资建设 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |