牌号简介 About |
---|
软性和非卤化阻燃挤出级,用于评估UL 62 SPE和Nispe配置的电缆护套等应用。阻燃性能满足UL 1581 VW-1要求。90C或105C温度等级由UL 62 TPE类别定义。85肖氏A硬度。通常在标准挤压设备上进行的加工。使用0.12 mm x 20绞合铜导线在2.0 mm电线上进行的UL 1581试验。 Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as cable jacket of UL 62 SPE and NISPE configurations. Flame retardant performance capable of meeting UL 1581 VW-1 requirement. 90C or 105C temperature rating as defined by UL 62 TPE category. 85 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.01 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,10.0kg 250℃,10.0kg |
16 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -40.0 | ℃ | ASTM D746 |
Heat Deformation(121℃) Heat Deformation(121℃) 8 |
5.0 | % | UL 1581 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
1.9E+16 | ohms·cm | ASTM D257 |
介电强度 Dielectric strength |
|||
2 mm,在油中 2 mm in oil |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
VW-1 VW-1 3 |
UL 1581 | ||
烟雾密度 Smoke density 9 |
|||
Flaming,Ds max:500.0 µm Flaming,Ds max:500.0 µm |
|||
Non-Flaming,Ds max:500.0 µm Non-Flaming,Ds max:500.0 µm |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,30 秒 Shore A, 30 seconds |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture 3 |
MPa | UL 1581 | |
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 5 |
MPa | UL 1581 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 3 |
% | UL 1581 | |
断裂 fracture 4 |
% | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 6 |
% | UL 1581 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 7 |
|||
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 |
备注 |
---|
3. 2.0 mm wire with 0.12 mm x 20 stranded copper |
4. 类型 1, 50 mm/min |
5. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
6. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
7. 13 mm/min |
8. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
9. Plaque |
【新闻资讯】查看全部
戴手套吃小龙虾,为何还是满手油?
2021-08-09 搜料网资讯: 消暑美味小龙虾,奈何两手油汪汪。 带上手套不沾油,仍是黄粱梦一场。 目前正值吃小龙虾的季节,在大快朵颐的时候,有个问题不知道大家注意过没有,为什么我明明 |
戴手套吃小龙虾,为何还是满手油? 搜料网资讯:消暑美味小龙虾,奈何两手油汪汪。 带上手套不沾油,仍是黄粱梦一场。 目前正值吃小龙虾的季节,在大快朵颐的时候,有个问题不知道大家注意过没有,为什么我明明带着手套吃小龙虾,手套没破,但手还是油腻腻的。
湖南科技大学化学化工学院教授陈建介绍,一般吃小龙虾的手套是PE材料制成,也就是俗称的聚乙烯,这是一种高分子材料,PE材料的分子结构是长长的链状,和油的分子结构十分类似。在化学上,有个专业术语叫做“相似相溶”,是指分子结构相同的物质可以相溶,就像海绵吸水一样,油可以“钻进”PE 手套里,相互融入。而手套薄薄的,自然又从另一面扩散出来粘在了手上。 另外,如今的塑料制品为减少环境污染,有些已经采用易分解设计,所以塑料手套看起光滑,但也有微小的孔,这就是为了方便降解。而这也是油能渗进手套的原因。 这么说来,戴手套并不能保持手部清洁,以后要不还是直接上手?不!专家建议还是带手套。 首先,油是少量渗入,效果还是比不戴手套好,更重要的是,PE手套可以防止吃到手上、指甲里的细菌。也就是说,你以为你带手套是为了防油,其实是防细菌。 湖南省产商品质量监督检验研究院的赵金尧研究员表示,针对PE手套,市场监管部门会检验总迁移量、微生物等,但在质量方面,对防油没要求。也就是说,PE手套本来就没义务帮你防油。 那么如何在吃小龙虾的时候,不要让手那么油腻呢? 以下做法仅供参考: 一是勤换手套。在油还没来得及进入手套时,迅速更换下一双手套。但缺点是费手套,不环保。 二是多带几层手套。根据油会渗透的原理,如果不想勤换,那就多戴几层手套。缺点是手会很热,油还没进入手套,手汗已经让你手套内壁黏糊糊了,而且也不环保。 三是手洗干净。边吃边洗手。缺点是太费水,没了大快朵颐的快感。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。