| 牌号简介 About |
|---|
| Alathon® H4250是一种高流动性冷冻级树脂，具有增强的低温冲击性能、增强的加工和热稳定性，具有良好的颜色和感官性能。典型的应用是刚性食品容器，如四、五和六夸脱的冰淇淋容器，在快速循环的多腔模具中高速生产。 Alathon H4250 is a high-flow "freezer" grade resin that exhibits enhanced cold temperature impact performance, enhanced processing and thermal stability, with good color and organoleptic properties. Typical applications are rigid food containers such as four, five and six-quart ice cream containers that are produced at high speeds in fast cycling multi-cavity stack molds. |
产品描述 Product Description
用途：薄壁容器;包装;容器;食品容器;硬包装;
加工条件：注射成型 Injection Molding
性能特点： 热稳定性好; 成型周期快; 着色性好; 耐低温冲击; 流动性高; 感官性好; 易加工; Excellent Processability,High liquidity,Quick molding cycle,Good sensory characteristics.,low-temperature impact resistance,Heat Stabilized,Good coloring
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density 2 |
0.942 | g/cm³ | ASTM D1505 |
|
表观密度 Apparent density |
0.59 到 0.63 | g/cm³ | ASTM D1895 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
50 | g/10min | ASTM D1238 |
|
螺旋流动长度 Spiral flow length |
43.7 | cm | 内部方法 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
35 | J/m | ASTM D256 |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
-18℃ -18℃ |
ASTM D4812 | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
结晶峰温度 Crystallization peak temperature |
|||
|
DSC DSC |
℃ | ASTM D3418 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ASTM D2240 | ||
|
拉伸模量 Tensile modulus |
|||
|
1% 正割 1% secant |
MPa | ||
|
拉伸强度 tensile strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
MPa | ||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
屈服，23℃ Yield, 23 ℃ |
% | ||
|
断裂，23℃ Fracture, 23 ℃ |
% | ||
|
弯曲模量 Bending modulus |
|||
|
-- -- |
MPa | ||
|
1% 正割 1% secant |
MPa | ||
|
2% 正割 2% secant |
MPa | ||
| 备注 |
|---|
| 2. 23°C |
|
【新闻资讯】查看全部 
中石油自主研发的极低密度聚乙烯树脂成功工业化生产
2020-11-19 搜料网资讯： 11月初，由石油化工研究院自主研发的极低密度聚乙烯热收缩膜专用料DQVL0810生产技术，在大庆石化塑料厂7.8万吨/年线性低密度聚乙烯工业装置上成功实现首次工业化应用 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |