牌号简介 About |
---|
Technyl Star S 60x1 V30 Natural是一种基于非卤化阻燃系统和专利的高流动性聚酰胺6树脂(TechnylStar)的等级,增强了30%的玻璃纤维,热稳定,用于注塑成型。这一等级是热稳定的,并提供优化的注塑性能。 TECHNYL STAR® S 60X1 V30 Natural is a grade based on a non-halogenated flame retardant system and on a patented high flow polyamide 6 resin (TechnylStar), reinforced of 30% of glass fiber, heat stabilized, for injection moulding. This grade is Heat stabilized and provides optimized injection moulding performance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.42 | g/cm³ | ISO 1183 |
吸水率 Water Absorption Water Absorption |
|||
24 h,23℃ 24 h,23℃ |
0.9 | % | ISO 62 |
|
4.2 | % | ISO 62 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
平行 parallel,72 h,23℃,50% r.h. Parallel, 72 hours, 23 ℃, 50% r. h |
0.25 | % | ISO 294-4 |
法向 normal,72 h,23℃,50% r.h. Normal, 72 hours, 23 ℃, 50% r. h |
0.8 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
干燥 dry Dry |
MPa | ISO 527 | |
湿润 cond. Wet Cond |
MPa | ISO 527 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
断裂 brk,干燥 dry Broken BRK, dry dry |
MPa | ISO 527-2 | |
断裂 brk,湿润 cond. Broken BRK, wet Cond |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,干燥 dry Broken BRK, dry dry |
% | ISO 527 | |
断裂 brk,湿润 cond. Broken BRK, wet Cond |
% | ISO 527 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
干燥 dry Dry |
MPa | ISO 178 | |
湿润 cond. Wet Cond |
MPa | ISO 178 | |
干燥 dry Dry |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
干燥 dry Dry |
MPa | ISO 178 | |
湿润 cond. Wet Cond |
MPa | ISO 178 | |
干燥 dry Dry |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179/1eU | |
23℃,湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179/1eU | |
-30℃,干燥 dry -30 ℃, dry |
kJ/m² | ISO 179/1eU | |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179/1eA | |
23℃,湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179/1eA | |
-30℃,干燥 dry -30 ℃, dry |
kJ/m² | ISO 179/1eA | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
23℃,干燥 dry 23 ℃, dry |
KJ/m² | ISO 180/1U | |
23℃,湿润 cond. 23 ℃, moist cond |
KJ/m² | ISO 180/1U | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃,干燥 dry 23 ℃, dry |
KJ/m² | ISO 180/1A | |
23℃,湿润 cond. 23 ℃, moist cond |
KJ/m² | ISO 180/1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.80 MPa 1.80 MPa |
℃ | ISO 75-1/-2 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
ohm·m | IEC 62631-3-1 | |
表面电阻率 Surface Resistivity Surface Resistivity |
ohm | IEC 62631-3-1 | |
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
V | IEC 60112 | |
介电强度 Dielectric Strength Dielectric Strength |
kV/mm | IEC 60243-1 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
0.75 mm 0.75 mm |
UL 94 | ||
1.5 mm 1.5 mm |
UL 94 | ||
3.0 mm 3.0 mm |
UL 94 | ||
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) Glow Wire Flammability Index (GWFI) |
|||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Glow Wire Ignitability Temperature(GWIT) Glow Wire Ignitability Temperature (GWIT) |
|||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Oxygen Index Oxygen Index |
% | ISO 4589-2 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部 |
搜料揭秘:听老司机讲汽车上的塑料零件 汽车上那些塑料零件,虽然从外观上看上去都差不多,但性能上相差甚远,听听搜料网老司机怎么说。
一、汽车保险杠
保险杠材料的选择原则 保险杠一般采用喷涂处理,长期受到风吹、日晒、雨淋,发生碰撞时首当其冲,所以其材料有以下要求: ▶ 良好的抗冲击性能:碰撞时有良好的弹性,为乘客提供保护; ▶ 良好的耐候性:防止在高温暴晒下变形、老化等;
▶ 良好的油漆附着能力:保证油漆不脱落、变色。
二、进气格栅
进气格栅材料选择原则 由于进气格栅靠近发动机舱,经常受到高温的烘烤,一般是电镀件,其材料有以下要求: ▶ 良好的电镀性能,有利于电镀; ▶ 良好的耐候性,防止在高温暴晒下变形、老化等;
▶ 良好的尺寸稳定性,在长期的工作中不能变形。
三、仪表板用料
仪表板材料选择原则 ▶ 良好的耐候性:防止在高温暴晒下变形、老化等;
▶ 良好的加工性能:便于注塑模具设计。
四、汽车车灯
汽车车灯材料的选择原则 ▶ 良好的耐冲击性能:能够承受一些调皮的小石子考验; ▶ 良好的透光性:雾度; ▶ 良好的耐候性:经受的起风吹、日晒、雨淋;
▶ 良好的稳定性:灯光炙烤下不能变形。
这些车用塑料不是我们生活中的普通塑料,不能下意识的把它们与廉价、不安全划上等号。它们都是由全球知名厂家,如SABIC沙伯基础、巴斯夫、拜耳、杜邦、LG、陶氏等生产的具有特殊性能的工程塑料。如果你对“橡塑世界”产生好奇,欢迎来“搜料网”。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。