牌号简介 About |
---|
Cycoloy CE3510聚碳酸酯/丙烯腈-丁二烯-苯乙烯(PC/ABS)树脂是一种可以注塑或挤压成板材进行二次热成型操作的树脂。这种无氯化、无溴阻燃PC/ABS具有UL V0阻燃等级。Cycoloy CE3510树脂是一种通用树脂,适用于各种应用,包括电缆通道,并通过DIN VDE 0472/815标准验证无卤素。 CYCOLOY CE3510 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a grade that can be injection molded or extruded into sheet for secondary thermoforming operations. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 flame rating. CYCOLOY CE3510 resin is a general purpose resin that is an excellent candidate for a wide variety of applications including cable channels and is verified non-halogen by the DIN VDE 0472/815 standard. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC+ABS PC+ABS
用途:电气/电子应用领域;汽车领域的应用;照明应用;Rail Applications;建筑应用领域;
加工条件:型材挤出成型 Profile extrusion
性能特点: 无卤; 耐高温; 阻燃; 冲击性能好; 易加工; Excellent Processability,High impact resistance,Halogen free,Flame Characteristics,High Heat Resistance
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.20 | g/cm³ | ASTM D792 |
-- -- |
1.21 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
8.00 | cm³/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 3 |
2680 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
屈服 yield 4 |
64.0 | MPa | ASTM D638 |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
-- -- 6 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 6 , 7 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 8 |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 9 |
kJ/m² | ISO 180-1A | |
0℃ 0℃ 9 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 9 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 9 |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Be | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Ae | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
73~77℃ 73~77℃ |
IEC 60695-10-2 | ||
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
0.8 mm,在油中 0.8 mm in oil |
kV/mm | ||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.75 mm 0.75 mm |
|||
1.50 mm 1.50 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1 mm 1 mm |
℃ | ||
1.5 mm 1.5 mm |
℃ | ||
3 mm 3 mm |
℃ |
备注 |
---|
3. 50 mm/min |
4. 类型 1, 50 mm/min |
5. 1.3 mm/min |
6. 2.0 mm/min |
7. at Yield |
8. 80*10*4 sp=62mm |
9. 80*10*4 mm |
10. 120*10*4 mm |
【新闻资讯】查看全部
南京工程海南乙烯项目脱碳五塔吊装就位
2021-10-12 搜料网资讯: 10月7日晚,南京工程公司EPC总承包的海南炼化乙烯C8联合装置首台设备脱碳五塔整体吊装就位,拉开了项目大型设备安装的序幕,标志着项目全面进入设备安装施工新阶段 |
南京工程海南乙烯项目脱碳五塔吊装就位 搜料网资讯:10月7日晚,南京工程公司EPC总承包的海南炼化乙烯C8联合装置首台设备脱碳五塔整体吊装就位,拉开了项目大型设备安装的序幕,标志着项目全面进入设备安装施工新阶段。 据了解,C8联合装置将一套新建55万吨/年裂解汽油加氢装置和一套35万吨/年芳烃抽提装置,共有11台大型塔器。本次吊装的脱碳五塔直径3.5米、高45米、重约67吨,是该装置首台大型模块化整体吊装设备。 项目部从前期图纸设计、塔器板材采购、塔内件资料的反馈、制造图纸的交付、后期大件运输等,进行了精心的策划和周密的计划安排,保证设备按时到现场。到场后,项目部以模块为单位进行深度预制、组装、调试和验收,实现了专业间的深度衔接配合。 为了减少高处作业和安全风险,提高工作效率,项目部按照模块化施工策划并结合现场具体情况,组织人员在地面完成劳动保护、管支架安装、塔体防腐保温等工作,电仪专业密切配合,加班加点完成电气灯具安装、电缆敷设、接线试照、前期基础验收和处理等工作。 当天19时,在起重人员的指挥下,设备在基础上顺利就位。随着临时电源接通,塔体照明灯发出耀眼的光芒,实现“穿衣戴帽、塔起灯亮”既定目标。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。