牌号简介 About |
---|
polifil gfpcc-ws系列化合物是用化学耦合玻璃纤维增强的水安全型均聚聚丙烯,通过NSF/ANSI标准61认证,满足美国和加拿大对饮用水系统组件的监管要求。与传统玻璃纤维增强聚丙烯相比,这些化合物具有优越的强度和刚度、改进的高温性能、更好的抗蠕变、更高的冲击强度和更高的耐高温水性。这些化合物用于耐化学性应用、电器、电气部件、汽车、灌溉、公用事业、过滤系统和饮用水产品。适用标准加工技术。使用此信息作为指南,帮助您选择适合您应用的树脂。 Polifil ® GFPPCC-WS series compounds are Water Safe Homopolymer polypropylenes reinforced with chemically coupled glass fibers and are certified to NSF/ANSI Standard 61 and meet the regulatory requirements of the U.S. and Canada for Drinking Water System Components. These compounds offer superior strength and stiffness, improved elevated temperature performance, better creep resistance, higher impact strength and higher resistance to high temperature water than conventional glass fiber reinforced polypropylenes. These compounds are used in chemical resistance applications, appliances, electrical components, automotive, irrigation, utility, filter systems, and potable water products. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
5.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:2.49 mm MD:2.49 mm |
0.40 | % | |
TD:2.49 mm TD:2.49 mm |
1.0 | % | |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.030 | % | ASTM D570 |
灰份含量 Ash Content |
% | ASTM D2584 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
正切,23℃ Tangent, 23 ℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
赢创扩展澳洲的膜产品消费
2016-10-09 化学品公司赢创已经扩大了其在澳洲的膜生产设备。赢创将提供它的高分子基膜科技用于气体分离和净化厂来作为这个科技公司-林德集团的工程部门。 这两个公司于今年八月开始合作,他们在Mankota(加拿大)利用膜的咋花流程和变压吸附科技提供氦净化服务。 托拜厄斯・凯勒是林德工程部的吸附和膜工程生产线的负责人,他说,“赢创的高选择性膜与我们其他已经确立的气体分离技术,比如我们世界一流的吸附技术, 允许我们在发展和应用新的更有效的净化工艺时拥有更多的灵活性。因此我们会加强 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |