Corton® 1085 HS 70104是一种40%滑石填充均聚聚丙烯化合物。它是为刚性部件开发的一种高流动注射成型等级,并稳定以满足汽车长期热老化要求。 Corton 1085 HS 70104 is a 40% talc filled homopolymer polypropylene compound. It is a high flow injection moulding grade developed for rigid components and is stabilized to meet long term automotive heat ageing requirements. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
19 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.0 mm MD:3.0 mm |
0.70 到 0.90 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3mm 3mm |
20 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3 mm 3 mm |
210 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.0 mm 0.45 MPa, unannealed, 3.0 mm |
℃ | ||
1.8 MPa,未退火,3.00 mm 1.8 MPa, unannealed, 3.00 mm |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~30℃,3.00 mm MD:-30~30℃,3.00 mm |
1/℃ | ASTM D696 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3.00 mm Shore D, 3.00 mm |
|||
邵氏 D,15 秒,3.00 mm Shore D, 15 seconds, 3.00 mm |
|||
洛氏硬度 Rockwell hardness |
|||
R 级,3.00 mm R-grade, 3.00 mm |
ASTM D785 | ||
拉伸强度 tensile strength 2 |
|||
3 mm 3 mm 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂,3 mm Fracture, 3 mm 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3 mm 3 mm |
MPa | ASTM D790 |
备注 |
---|
2. 50 mm/min |
【新闻资讯】查看全部
越南扩大对欧盟出口塑料制品
2021-04-20 搜料网资讯: 近日,有官方数据显示,越南的塑料制品出口中,对欧盟的出口占到出口总额的18.2%。分析称,去年8月生效的欧盟-越南自由贸易协定(EVFTA)为促进塑料领域的出口和投资带 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |