牌号简介 About |
---|
NEOFLON® FEP NP-112是以提高应力抗裂性和提高挤出速度而研制的,用于电器线、阻燃电缆绝缘、管材、薄膜等金属线绝缘的挤出,也可用于薄壁件的注塑成型。 Neoflon® FEP NP-112 was developed with improved stress crack resistance and improved extrusion speed for extrusion of wire insulation for appliance wire, plenum cable insulation, tubing, and film, etc. It may also be used for injection molding of thin wall parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
372℃,2.16kg 372℃,2.16kg |
9.0 到 14 | g/10min | ASTM D2116 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
> 20.0 | MPa | ASTM D2116 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
> 300 | % | ASTM D2116 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature 2 |
250 到 265 | ℃ | ASTM D2116 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
MIT耐折强度(周期) MIT flexural strength (cycle) |
15000 | ASTM D2176 |
备注 |
---|
2. DSC |
【新闻资讯】查看全部
高性能聚丁二烯橡塑复合新材料开发取得成功
2020-12-08 搜料网资讯: 日前,高性能聚丁二烯橡塑复合新材料开发取得成功,填补国内空白。 该项目由燕山石化和北京化工大学联合开发,聚丁二烯橡塑复合材料是现在高顺式橡胶的升级换代产 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |