牌号简介 About |
---|
ET509B是一种采用SCLAIRTECH技术生产的黑色高密度聚乙烯。采用熔融共混法对其进行了很好的改性,满足了GLOBLA标准和客户自己的标准要求。它被设计为在3层管道涂层系统中使用传统的嫁接粘合剂(Polyglue LE149V、LE200T、LE100A和LE851P等)作为面漆。ET509B基聚乙烯具有高物理性能,来源于高密度聚乙烯(HDPE),共混树脂改善了ESCR性能、冲击性能和加工性能。ET509B与三层PE的聚乙烯等级一起,显示了适用于所有管道涂层规范的高度调整管道涂层系统,包括DIN30670、CSA Z425.21-02、NFA 49-710。 ET509B is a black, high-density polyethylene produced with Sclairtech technology. It is well modified by melt blending to meet the requirements of globla standards and standards of customers' own. It is designed for use as a top-coat in 3-layer pipe coating systems with conventional grafted adhesive (Polyglue LE149V, LE200T, LE100A and LE851P etc). Base PE of ET509B has high physical properties originated from HDPE and blended resins improve ESCR, impact properties and processibility. Together with Polyglue grades for 3-layer PE, ET509B shows highly adjusted pipe coating system available for all pipe coating specification including DIN30670, CSA Z425.21-02, NFA 49-710. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.949 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.30 | g/10min | ASTM D1238 |
吸水率 Water absorption rate |
|||
24hr 24hr |
< 0.010 | % | ASTM D570 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
10%非离子表面活性剂,F50 10% non-ionic surfactant, F50 |
> 1000 | hr | ASTM D1693 |
炭黑含量 Carbon black content |
> 2.0 | wt% | ASTM D1603 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
氧感应时间 Oxygen sensing time |
|||
220℃ 220℃ |
min | ASTM D3895 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
研究人员将植物废料转化为生物基多元醇,用于聚氨酯保温材料
2023-02-01 扫描上图二维码,可以免费下载 搜料 APP 土耳其的一组研究人员在埃斯基希尔理工大学实验室通过甜菜浆、番茄、胡椒、薰衣草、百里香浆、豌豆、红芸豆荚和其他植物材料的液化生产 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |