这种茂金属线性低密度聚乙烯是一种乙烯-己烯共聚物,为吹塑薄膜应用量身定制,要求:高清晰度、优异的光泽、优异的韧性、优异的热密封、典型的吹塑薄膜应用包括:共挤中的密封层、重型包装透明包装。 This metallocene linear low density polyethylene is an ethylene-hexene copolymer tailored for blown film applications that require: Superb clarity Excellent gloss Exceptional toughness Outstanding heat seal Typical blown film applications include: Seal layer in coextrusions Heavy duty packaging Clarity packaging |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
> 1.0 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus |
|||
1% 正割,MD:25 µm,吹塑薄膜 1% secant, MD: 25 µ m, blow molded film |
179 | MPa | |
1% 正割,TD:25 µm,吹塑薄膜 1% secant, TD: 25 µ m, blow molded film |
MPa | ||
拉伸强度 tensile strength |
|||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ||
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ||
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ||
始封温度 Initial sealing temperature 2 |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film 2 |
℃ | ASTM F88 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,25.4 µm,吹塑薄膜 60 °, 25.4 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
2. Temperature at which 0.3 lb/in heat seal strength is achieved. 0.5 s dwell, 30 psi pressure, 11.8 in/min separation rate. |
【新闻资讯】查看全部
十年“限塑令”效果遭疑 治理白色污染前路如何?
2018-01-19 近期,国家发改委向社会征集塑料垃圾污染防治的建议,“限塑令”发布十年后,中国治理“白色污染”的成效再度引发舆论热议。 一方面是社会对“限塑令”效果的质疑,一方面是快递、外卖等新业态对塑料包装的刚需,中国与“白色污染”的拉锯战前路如何? 发改委:正研究制定防治塑料垃圾污染的政策 近日,国家发改委网站发布《我为塑料垃圾污染防治建言献策》的消息,邀请社会各界围绕不同领域塑料制品的管理要求,提出意见建议。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |