牌号简介 About |
---|
大金聚四氟乙烯F-207是一种不使用全氟辛酸(PFOA)生产的用于膏体挤出的聚四氟乙烯细粉末树脂。F-207是为小直径同轴电缆和管道应用而设计的,这些应用在高减速比下运行。F-207具有较低、均匀的介电常数和较宽的频率范围内的损耗因数,是高频绝缘应用的理想选择。F-207还具有良好的热稳定性和在低挤压压力下的良好尺寸公差。 Daikin PTFE F-207 is a polytetrafluoroethylene fine powder resin for paste extrusion manufactured without the use of PFOA. F-207 has been designed for small diameter coaxial cables and tubing applications that are run at high reduction ratios. F-207 is ideal for high frequency insulating applications because of its low, uniform dielectric constant and dissipation factor over a wide frequency range. F-207 also demonstrates good thermal stability and excellent dimensional tolerance at low extrusion pressures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.16 到 2.17 | g/cm³ | ASTM D4895 |
表观密度 Apparent density |
0.45 到 0.55 | g/cm³ | ASTM D4895 |
颗粒大小 Particle size |
400 到 650 | µm | ASTM D4895 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
> 25.0 | MPa | ASTM D4895 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
> 300 | % | ASTM D4895 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
挤出压力 Extrusion pressure |
MPa | 内部方法 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
雪佛龙承诺减缓碳排放,以适度的支出提高石油产量
2021-03-12 搜料网资讯: 雪佛龙概述了一项到2025年扩大油气产量的计划,并承诺限制碳排放的增长速度,但不会大幅增加支出。 疫情封锁导致的能源需求下降,使该行业在2020年陷入困境,并导致 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |