| 牌号简介 About |
|---|
| 无铅热塑性CPE化合物ThermodanCP 0110-108 BK是一种黑色、抗紫外线、无铅、符合RoHS标准的热塑性CPE化合物。它设计用于各种护套应用，包括电线、电缆和管束。该化合物具有火焰传播慢、自熄等优良的燃烧性能。THERMODAN® CP 0110-108 BK应采用螺杆结构挤压，以优化工艺条件和生产能力。这种挤压复合材料符合或超过几个工业护套规范，包括UL 1277电缆槽。 Lead-free Thermoplastic CPE compound THERMODAN®CP 0110-108 BK is a black, UV resistant, lead-free, RoHS compliant, thermoplastic CPE compound. It is designed for use in a wide variety of jacketing applications including wire and cable and tube bundles. This compound has superior fire performance, including slow flame propagation, and self-extinguishing characteristics. THERMODAN® CP 0110-108 BK should be extruded with a screw configuration designed to optimize process conditions and throughput. This extrusion compound meets, or exceeds, several industry jacketing specifications, including UL 1277 tray cable. |
产品描述 Product Description
用途：护套;电线电缆应用;管件;
加工条件：挤出 Extrusion
性能特点： 无铅; 自熄; 耐候抗UV; Weather resistance is good,Self-extinguishing,Lead content is low to none
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density 2 |
1.37 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，21.6kg 190℃，21.6kg |
6.0 | g/10min | ASTM D1238 |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
撕裂强度 tear strength 2 |
|||
|
开裂 cracking 2 |
67 | kN/m | ASTM D470 |
|
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度的变化率 The rate of change in tensile strength |
|||
|
75℃，1440 hr，in Oil 75℃，1440 hr，in Oil |
80 | % | |
|
100℃，96 hr，in Oil 100℃，96 hr，in Oil |
65 | % | |
|
121℃，168 hr 121℃，168 hr |
% | ||
|
极限伸长率的变化率 Change rate of ultimate elongation |
|||
|
75℃，1440 hr，在油中 75 ℃, 1440 hr, in oil |
% | ||
|
100℃，96 hr，在油中 100 ℃, 96 hr, in oil |
% | ||
|
121℃，168 hr 121℃，168 hr |
% | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature 3 |
℃ | ASTM D746 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A，1 秒 Shore A, 1 second |
|||
|
邵氏 D，10 秒 Shore D, 10 seconds |
|||
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
1% 正割 1% secant |
MPa | ASTM D790 | |
|
负载变形 Load deformation |
|||
|
100℃，0.20 MPa 100℃，0.20 MPa |
% | ||
|
121℃，0.20 MPa 121℃，0.20 MPa |
% | ||
| 备注 |
|---|
| 2. 23°C |
| 3. 3min in methanol |
|
【新闻资讯】查看全部
Kordsa计划收购英威达Chattanooga工厂大部分业务
2016-12-27 尼龙纤维制造商英威达在努力削减Chattanooga工厂产量的时候，工厂内的另一家公司却计划着要买下英威达的生产场地和其它设施。 Kordsa北美人力资源和信息技术经理 Mark Myers星期三的时候透露Kordsa和英威达在谈判这一收购行动，将占英威达目前生产使用面积的较大部分。交易有望在2017年第一季度完成。 Kordsa在 Access Road工厂的员工约有190人，这一工厂最初是由杜邦建筑运营的。 英威达母公司科氏工业集团今年夏 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付