牌号简介 About |
---|
30%玻璃纤维增强,薄壁溴化阻燃,高流量,高CTI 30% glass fiber reinforced, thin wall brominated FR, high flow, high CTI |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.67 | g/cm³ | ASTM D792 |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,5 kg 250℃,5 kg |
28.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.30 | % | |
TD TD |
0.70 | % | |
吸水率 Water absorption rate 3 |
|||
23℃,24hr 23℃,24hr 3 |
0.24 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 4 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 5 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 5 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield 5 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- 7 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 7 , 8 |
MPa | ISO 178 | |
断裂,50 mm跨度 Fracture, 50 mm span 6 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/2U | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 9 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 9 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 9 |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm,64 mm跨距 1.8 MPa, unannealed, 4.0 mm, 64 mm span 9 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test 11 |
|||
190℃ 190℃ 11 |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:23~80℃ TD:23~80℃ |
1/℃ | ASTM E831 | |
TD:-40℃ TD:-40℃ |
1/℃ | ISO 11359-2 | |
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) 12 |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.28 mm 0.28 mm |
|||
1.50 mm 1.50 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
0.4 mm 0.4 mm |
℃ | ||
0.8 mm 0.8 mm |
℃ | ||
1 mm 1 mm |
℃ | ||
2 mm 2 mm |
℃ | ||
3 mm 3 mm |
℃ | ||
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
3. Internal Method |
4. 5.0 mm/min |
5. 类型 1, 5.0 mm/min |
6. 1.3 mm/min |
7. 2.0 mm/min |
8. at Break |
9. 80*10*4 mm |
10. 速率 A (50°C/h), 载荷2 (50N) |
11. Approximate Maximum |
12. Surface |
【新闻资讯】查看全部
美股涨!欧股涨!油价涨!金价涨!什么情况?
2021-05-10 搜料网资讯: 美股涨!欧股涨!油价涨!金价涨!什么情况? 当地时间周五,美国股市三大股指连续第二个交易日,也是本周第二次集体收涨,其中,道指上涨0.66%,收于34777.76点,再 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |