牌号简介 About |
---|
符合ISO 1043-1的材料规范:30%长玻璃纤维增强聚丙烯共聚物。低排放。纤维与聚丙烯基体发生化学耦合。球是圆柱形的,通常也包括10 mm长的嵌入纤维。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架,因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型,可以制造出具有高再现性的复杂零件。应用领域:汽车功能/结构件 Material code according to ISO 1043-1: PP Polypropylene copolymer reinforced with 30weight percent long glass fibers. Low emission. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.12 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
6200 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
断裂 fracture |
100 | MPa | ISO 527-2/1A/5 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.5 | % | ISO 527-2/1A/5 |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
6000 | MPa | |
80℃ 80℃ |
MPa | ||
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ||
80℃ 80℃ |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
国际金价高点回落,投行称现在“下车”为时尚早
2022-03-23 早前乌克兰局势的恶化一度使金价飙升,而追逐动能的CTA策略(商品投资顾问)更是大力做多,将金价推上两年高点2070美元/盎司。但上周随着局势变化以及多头获利了结,金价与其他 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |