| 牌号简介 About |
|---|
| 符合ISO 1043-1的材料规范：聚丙烯热稳定聚丙烯，用50%重量%长的玻璃纤维加固。该产品排放量低。纤维与聚丙烯基体发生化学耦合。球是圆柱形的，通常也包括10 mm长的嵌入纤维。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架，因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型，可以制造出具有高再现性的复杂零件。应用领域：汽车功能/结构件 Material code according to ISO 1043-1: PP Heat stabilized polypropylene reinforced with 50 weight percent long glass fibers. The product has low emissions. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
产品描述 Product Description
用途：汽车领域的应用;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 化学耦合; 热稳定性好; 低VOC; 耐低温冲击; 各向同性好; 低翘曲性; 韧性好; Low warping,low-temperature impact resistance,Good Isotropy,Good Rigidity,Chemical coupling,Low odor,Heat Stabilized,Good flexibility
填料：玻璃纤维 50
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density Density |
1.34 | g/cm³ | ISO 1183 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus Tensile modulus |
11600 | MPa | ISO 527-2/1A |
|
拉伸应力 Tensile stress Tensile stress |
|||
|
断裂 break Break |
140 | MPa | ISO 527-2/1A/5 |
|
拉伸应变 Tensile strain Tensile strain |
|||
|
断裂 break Break |
1.8 | % | ISO 527-2/1A/5 |
|
弯曲模量 Flexural modulus Flexural modulus |
|||
|
23℃ 23℃ |
12000 | MPa | |
|
80℃ 80℃ |
MPa | ||
|
弯曲强度 Flexural strength Flexural strength |
|||
|
23℃ 23℃ |
MPa | ||
|
80℃ 80℃ |
MPa | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy impact strength Charpy impact strength |
|||
|
-30℃ -30℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
简支梁无缺口冲击强度 Charpy notched impact strength Charpy Unnotch Impact strength |
|||
|
-30℃ -30℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT Hot deformation temperature HDT |
|||
|
1.8 MPa，未退火 unannealed 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
8.0 MPa，未退火 unannealed 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
1.00 mm 1.00 mm |
UL 94 | ||
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
介电常数 Dielectric Constant Dielectric Constant |
|||
|
10 MHz 10 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation Factor Dissipation Factor |
|||
|
10 MHz 10 MHz |
E-4 | IEC 60250 | |
| 备注 |
|---|
| 2. 10°C/min |
|
【新闻资讯】查看全部 
科莱恩医疗包装亮相世界制药原料中国展，强调区域制造
2016-06-28 全球领先的特种化学品制造商科莱恩携医疗包装业务部门出席了6月21日至23日在上海新国际博览中心举办的顶级区域性医药展览会――世界制药原料中国展(CPhI China)，重点展示其在中国的干燥剂和其他医疗包装产品的生产基地。同时，凭借将于2017年在印度启用的第三个生产设施，以及现有的位于美国和欧洲的工厂，科莱恩在区域制造领域的重大影响力将确保中国客户获得持续可靠的供应链。科莱恩医疗包装的展位号是W5G26。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付